Nondestructive testing

Nondestructive testing or non-destructive testing (NDT) is a wide group of analysis techniques used in science and technology industry to evaluate the properties of a material, component or system without causing damage.[1] The terms nondestructive examination (NDE), nondestructive inspection (NDI), and nondestructive evaluation (NDE) are also commonly used to describe this technology.[2] Because NDT does not permanently alter the article being inspected, it is a highly valuable technique that can save both money and time in product evaluation, troubleshooting, and research. The six most frequently used NDT methods are eddy-current, magnetic-particle, liquid penetrant, radiographic, ultrasonic, and visual testing.[3] NDT is commonly used in forensic engineering, mechanical engineering, petroleum engineering, electrical engineering, civil engineering, systems engineering, aeronautical engineering, medicine, and art.[1] Innovations in the field of nondestructive testing have had a profound impact on medical imaging, including on echocardiography, medical ultrasonography, and digital radiography.

Methods

NDT methods may rely upon use of electromagnetic radiation, sound, and inherent properties of materials to examine samples. This includes some kinds of microscopy to examine external surfaces in detail, although sample preparation techniques for metallography, optical microscopy and electron microscopy are generally destructive as the surfaces must be made smooth through polishing or the sample must be electron transparent in thickness. The inside of a sample can be examined with penetrating radiation, such as X-rays, neutrons or terahertz radiation. Sound waves are utilized in the case of ultrasonic testing. Contrast between a defect and the bulk of the sample may be enhanced for visual examination by the unaided eye by using liquids to penetrate fatigue cracks. One method (liquid penetrant testing) involves using dyes, fluorescent or non-fluorescent, in fluids for non-magnetic materials, usually metals. Another commonly used NDT method used on ferrous materials involves the application of fine iron particles (either liquid or dry dust) that are applied to a part while it is in an externally magnetized state (magnetic-particle testing). The particles will be attracted to leakage fields within the test object, and form on the objects surface. Magnetic particle testing can reveal surface & some sub-surface defects within the part. Thermoelectric effect (or use of the Seebeck effect) uses thermal properties of an alloy to quickly and easily characterize many alloys. The chemical test, or chemical spot test method, utilizes application of sensitive chemicals that can indicate the presence of individual alloying elements. Electrochemical methods, such as electrochemical fatigue crack sensors, utilize the tendency of metal structural material to oxidize readily in order to detect progressive damage.

Analyzing and documenting a nondestructive failure mode can also be accomplished using a high-speed camera recording continuously (movie-loop) until the failure is detected. Detecting the failure can be accomplished using a sound detector or stress gauge which produces a signal to trigger the high-speed camera. These high-speed cameras have advanced recording modes to capture some non-destructive failures.[4] After the failure the high-speed camera will stop recording. The capture images can be played back in slow motion showing precisely what happen before, during and after the nondestructive event, image by image.

Applications

NDT is used in a variety of settings that covers a wide range of industrial activity, with new NDT methods and applications, being continuously developed. Nondestructive testing methods are routinely applied in industries where a failure of a component would cause significant hazard or economic loss, such as in transportation, pressure vessels, building structures, piping, and hoisting equipment.

Weld verification

  1. Section of material with a surface-breaking crack that is not visible to the naked eye.
  2. Penetrant is applied to the surface.
  3. Excess penetrant is removed.
  4. Developer is applied, rendering the crack visible.

In manufacturing, welds are commonly used to join two or more metal parts. Because these connections may encounter loads and fatigue during product lifetime, there is a chance that they may fail if not created to proper specification. For example, the base metal must reach a certain temperature during the welding process, must cool at a specific rate, and must be welded with compatible materials or the joint may not be strong enough to hold the parts together, or cracks may form in the weld causing it to fail. The typical welding defects (lack of fusion of the weld to the base metal, cracks or porosity inside the weld, and variations in weld density) could cause a structure to break or a pipeline to rupture.

Welds may be tested using NDT techniques such as industrial radiography or industrial CT scanning using X-rays or gamma rays, ultrasonic testing, liquid penetrant testing, magnetic particle inspection or via eddy current. In a proper weld, these tests would indicate a lack of cracks in the radiograph, show clear passage of sound through the weld and back, or indicate a clear surface without penetrant captured in cracks.

Welding techniques may also be actively monitored with acoustic emission techniques before production to design the best set of parameters to use to properly join two materials.[5] In the case of high stress or safety critical welds, weld monitoring will be employed to confirm the specified welding parameters (arc current, arc voltage, travel speed, heat input etc.) are being adhered to those stated in the welding procedure. This verifies the weld as correct to procedure prior to nondestructive evaluation and metallurgy tests.

Structural mechanics

Structure can be complex systems that undergo different loads during their lifetime, e.g. Lithium-ion batteries.[6] Some complex structures, such as the turbo machinery in a liquid-fuel rocket, can also cost millions of dollars. Engineers will commonly model these structures as coupled second-order systems, approximating dynamic structure components with springs, masses, and dampers. The resulting sets of differential equations are then used to derive a transfer function that models the behavior of the system.

In NDT, the structure undergoes a dynamic input, such as the tap of a hammer or a controlled impulse. Key properties, such as displacement or acceleration at different points of the structure, are measured as the corresponding output. This output is recorded and compared to the corresponding output given by the transfer function and the known input. Differences may indicate an inappropriate model (which may alert engineers to unpredicted instabilities or performance outside of tolerances), failed components, or an inadequate control system.

Radiography in medicine

Chest radiography indicating a peripheral bronchial carcinoma.

As a system, the human body is difficult to model as a complete transfer function. Elements of the body, however, such as bones or molecules, have a known response to certain radiographic inputs, such as x-rays or magnetic resonance. Coupled with the controlled introduction of a known element, such as digested barium, radiography can be used to image parts or functions of the body by measuring and interpreting the response to the radiographic input. In this manner, many bone fractures and diseases may be detected and localized in preparation for treatment. X-rays may also be used to examine the interior of mechanical systems in manufacturing using NDT techniques, as well.

Notable events in early academic and industrial NDT

(Basic Source for above: Hellier, 2001) Note the number of advancements made during the WWII era, a time when industrial quality control was growing in importance.

Methods and techniques

An example of a 3D replicating technique. The flexible high-resolution replicas allow surfaces to be examined and measured under laboratory conditions. A replica can be taken from all solid materials.

NDT is divided into various methods of nondestructive testing, each based on a particular scientific principle. These methods may be further subdivided into various techniques. The various methods and techniques, due to their particular natures, may lend themselves especially well to certain applications and be of little or no value at all in other applications. Therefore, choosing the right method and technique is an important part of the performance of NDT.

Personnel training, qualification and certification

Successful and consistent application of nondestructive testing techniques depends heavily on personnel training, experience and integrity. Personnel involved in application of industrial NDT methods and interpretation of results should be certified, and in some industrial sectors certification is enforced by law or by the applied codes and standards.[14]

Definitions

The following definitions for qualification and certification are given in ISO 9712:[15]

In US standards and codes, while a very similar definition of qualification is included in ASNT SNT-TC-1A, certification is simply defined as: "Written testimony of qualification".

In the aerospace sector, EN 4179:2009 contains the following definitions:[16]

Training

Non-Destructive Testing (NDT) training is provided for people working in many industries. It is generally necessary that the candidate successfully completes a theoretical and practical training program, as well as have performed several hundred hours of practical application of the particular method they wish to be trained in. At this point, they may pass a certification examination. While online training has become more popular, many certifying bodies will require additional practical training.

Certification schemes

There are two approaches in personnel certification:[17]

  1. Employer Based Certification: Under this concept the employer compiles their own Written Practice. The written practice defines the responsibilities of each level of certification, as implemented by the company, and describes the training, experience and examination requirements for each level of certification. In industrial sectors the written practices are usually based on recommended practice SNT-TC-1A of the American Society for Nondestructive Testing.[18] ANSI standard CP-189 outlines requirements for any written practice that conforms to the standard.[19] For aviation, space, and defense (ASD) applications NAS 410 sets further requirements for NDT personnel, and is published by AIA - Aerospace Industries Association, which is made up of US aerospace airframe and powerplant manufacturers. This is the basis document for EN 4179[16] and other (USA) NIST-recognized aerospace standards for the Qualification and Certification (employer-based) of Nondestructive Testing personnel. NAS 410 also sets the requirements also for "National NDT Boards", which allow and proscribe personal certification schemes. NAS 410 allows ASNT Certification as a portion of the qualifications needed for ASD certification.[20]
  2. Personal Central Certification: The concept of central certification is that an NDT operator can obtain certification from a central certification authority, that is recognized by most employers, third parties and/or government authorities. Industrial standards for central certification schemes include ISO 9712,[15] and ANSI/ASNT CP-106[21] (used for the ASNT ACCP [22] scheme). Certification under these standards involves training, work experience under supervision and passing a written and practical examination set up by the independent certification authority. EN 473[23] was another central certification scheme, very similar to ISO 9712, which was withdrawn when CEN replaced it with EN ISO 9712 in 2012.

In the United States employer based schemes are the norm, however central certification schemes exist as well. The most notable is ASNT Level III (established in 1976-1977), which is organized by the American Society for Nondestructive Testing for Level 3 NDT personnel.[24] NAVSEA 250-1500 is another US central certification scheme, specifically developed for use in the naval nuclear program.[25]

Central certification is more widely used in the European Union, where certifications are issued by accredited bodies (independent organizations conforming to ISO 17024 and accredited by a national accreditation authority like UKAS). The Pressure Equipment Directive (97/23/EC) actually enforces central personnel certification for the initial testing of steam boilers and some categories of pressure vessels and piping.[26] European Standards harmonized with this directive specify personnel certification to EN 473. Certifications issued by a national NDT society which is a member of the European Federation of NDT (EFNDT) are mutually acceptable by the other member societies [27] under a multilateral recognition agreement.

Canada also implements an ISO 9712 central certification scheme, which is administered by Natural Resources Canada, a government department.[28][29][30]

The aerospace sector worldwide sticks to employer based schemes.[31] In America it is based mostly on AIA-NAS-410 [32] and in the European Union on the equivalent and very similar standard EN 4179.[16] However EN 4179:2009 includes an option for central qualification and certification by a National aerospace NDT board or NANDTB (paragraph 4.5.2).

Levels of certification

Most NDT personnel certification schemes listed above specify three "levels" of qualification and/or certification, usually designated as Level 1, Level 2 and Level 3 (although some codes specify Roman numerals, like Level II). The roles and responsibilities of personnel in each level are generally as follows (there are slight differences or variations between different codes and standards):[15][16]

Terminology

The standard US terminology for Nondestructive testing is defined in standard ASTM E-1316.[33] Some definitions may be different in European standard EN 1330.

Indication 
The response or evidence from an examination, such as a blip on the screen of an instrument. Indications are classified as true or false. False indications are those caused by factors not related to the principles of the testing method or by improper implementation of the method, like film damage in radiography, electrical interference in ultrasonic testing etc. True indications are further classified as relevant and non relevant. Relevant indications are those caused by flaws. Non relevant indications are those caused by known features of the tested object, like gaps, threads, case hardening etc.
Interpretation 
Determining if an indication is of a type to be investigated. For example, in electromagnetic testing, indications from metal loss are considered flaws because they should usually be investigated, but indications due to variations in the material properties may be harmless and nonrelevant.
Flaw 
A type of discontinuity that must be investigated to see if it is rejectable. For example, porosity in a weld or metal loss.
Evaluation 
Determining if a flaw is rejectable. For example, is porosity in a weld larger than acceptable by code?
Defect 
A flaw that is rejectable — i.e. does not meet acceptance criteria. Defects are generally removed or repaired.[33]

Reliability and statistics

Probability of detection (POD) tests are a standard way to evaluate a nondestructive testing technique in a given set of circumstances, for example "What is the POD of lack of fusion flaws in pipe welds using manual ultrasonic testing?" The POD will usually increase with flaw size. A common error in POD tests is to assume that the percentage of flaws detected is the POD, whereas the percentage of flaws detected is merely the first step in the analysis. Since the number of flaws tested is necessarily a limited number (non-infinite), statistical methods must be used to determine the POD for all possible defects, beyond the limited number tested. Another common error in POD tests is to define the statistical sampling units (test items) as flaws, whereas a true sampling unit is an item that may or may not contain a flaw.[34][35] Guidelines for correct application of statistical methods to POD tests can be found in ASTM E2862 Standard Practice for Probability of Detection Analysis for Hit/Miss Data and MIL-HDBK-1823A Nondestructive Evaluation System Reliability Assessment, from the U.S. Department of Defense Handbook.

See also

References

  1. 1 2 Cartz, Louis (1995). Nondestructive Testing. A S M International. ISBN 978-0-87170-517-4.
  2. Charles Hellier (2003). Handbook of Nondestructive Evaluation. McGraw-Hill. p. 1.1. ISBN 0-07-028121-1.
  3. Introduction to Nondestructive Testing, The American Society for Nondestructive Testing
  4. Bridges, Andrew. "High Speed Cameras for Non-Destructive Testing". NASA TechBriefs. Retrieved 1 November 2013.
  5. Blitz, Jack; G. Simpson (1991). Ultrasonic Methods of Non-Destructive Testing. Springer-Verlag New York, LLC. ISBN 978-0-412-60470-6.
  6. Waldmann, T. (2014). "A Mechanical Aging Mechanism in Lithium-Ion Batteries". Journal of the Electrochemical Society. 161: A1742. doi:10.1149/2.1001410jes.
  7. Introduction and History of Penetrant Inspection
  8. Singh S, Goyal A (2007). "The origin of echocardiography: a tribute to Inge Edler". Tex Heart Inst J. 34: 431–8. PMC 2170493Freely accessible. PMID 18172524.
  9. U.S. Patent 3,277,302, titled "X-Ray Apparatus Having Means for Supplying An Alternating Square Wave Voltage to the X-Ray Tube", granted to Weighart on October 4, 1964, showing its patent application date as May 10, 1963 and at lines 1-6 of its column 4, also, noting James F. McNulty’s earlier filed co-pending application for an essential component of invention
  10. U.S. Patent 3,289,000, titled "Means for Separately Controlling the Filament Current and Voltage on a X-Ray Tube", granted to McNulty on November 29, 1966 and showing its patent application date as March 5, 1963
  11. ASTM E1351: "Standard Practice for Production and Evaluation of Field Metallographic Replicas" (2006)
  12. BS ISO 3057 "Non-destructive testing - Metallographic replica techniques of surface examination" (1998)
  13. "Fundamentals of Resonant Acoustic Method NDT" (2005)
  14. "ICNDT Guide to Qualification and Certification of Personnel for NDT" (PDF). International Committee for NDT. 2012.
  15. 1 2 3 ISO 9712: Non-destructive testing -- Qualification and certification of NDT personnel (2012)
  16. 1 2 3 4 EN 4179: "Aerospace series. Qualification and approval of personnel for non-destructive testing" (2009)
  17. John Thompson (November 2006). Global review of qualification and certification of personnel for NDT and condition monitoring. 12th A-PCNDT 2006 – Asia-Pacific Conference on NDT. Auckland, New Zealand.
  18. Recommended Practice No. SNT-TC-1A: Personnel Qualification and Certification in Nondestructive Testing, (2006)
  19. ANSI/ASNT CP-189: ASNT Standard for Qualification and Certification of Nondestructive Testing Personnel, (2006)
  20. AIA NAS410
  21. ANSI/ASNT CP-106: "ASNT Standard for Qualification and Certification of Nondestructive Testing Personnel" (2008)
  22. "ASNT Central Certification Program", ASNT Document ACCP-CP-1, Rev. 7 (2010)
  23. EN 473: Non-destructive testing. Qualification and certification of NDT personnel. General principles, (2008)
  24. Charles Hellier (2003). Handbook of Nondestructive Evaluation. McGraw-Hill. p. 1.25. ISBN 0-07-028121-1.
  25. Charles Hellier (2003). Handbook of Nondestructive Evaluation. McGraw-Hill. p. 1.26. ISBN 0-07-028121-1.
  26. Directive 97/23/EC of the European Parliament and of the Council of 29 May 1997 on the approximation of the laws of the Member States concerning pressure equipment, Annex I, paragraph 3.1.3
  27. EFNDT/SEC/P/05-006: Agreement for EFNDT multilateral recognition of NDT personnel certification schemes (2005)
  28. http://www.nrcan-rncan.gc.ca/smm-mms/ndt-end/index-eng.htm : The NDT Certifying Agency (CANMET-MTL)
  29. The relevant national standard for Canada is CAN/CGSB-48.9712-2006 "Qualification and Certification of Non-Destructive Testing Personnel.", which complies with the requirements of ISO 9712:2005 and EN 473:2000.
  30. Charles Hellier (2003). Handbook of Nondestructive Evaluation. McGraw-Hill. p. 1.27. ISBN 0-07-028121-1.
  31. R. Marini and P. Ranos: "Current Issues in Qualification and Certification of Non-Destructive Testing Personnel in the Aerospace Industry", ECNDT 2006 - Th.3.6.5
  32. AIA-NAS-410: "Aerospace Industries Association, National Aerospace Standard, NAS Certification and Qualification of Nondestructive Test Personnel"
  33. 1 2 ASTM E-1316: "Standard Terminology for Nondestructive Examinations", The American Society for Testing and Materials, in Volume 03.03 NDT, 1997
  34. T. Oldberg and R. Christensen (1999). "Erratic Measure". 4 (5). NDT.net.
  35. T. Oldberg (2005). "An Ethical Problem in the Statistics of Defect Detection Test Reliability". 10 (5). NDT.net.

Bibliography

  • ASTM International, ASTM Volume 03.03 Nondestructive Testing
    • ASTM E1316-13a: "Standard Terminology for Nondestructive Examinations" (2013)
  • ASNT, Nondestructive Testing Handbook
  • Bray, D.E. and R.K. Stanley, 1997, Nondestructive Evaluation: A Tool for Design, Manufacturing and Service; CRC Press, 1996.
  • Charles Hellier (2003). Handbook of Nondestructive Evaluation. McGraw-Hill. ISBN 0-07-028121-1. 
  • Shull, P.J., Nondestructive Evaluation: Theory, Techniques, and Applications, Marcel Dekker Inc., 2002.
  • EN 1330: Non-destructive testing. Terminology. Nine parts. Parts 5 and 6 replaced by equivalent ISO standards.
    • EN 1330-1: Non-destructive testing. Terminology. List of general terms (1998)
    • EN 1330-2: Non-destructive testing. Terminology. Terms common to the non-destructive testing methods (1998)
    • EN 1330-3: Non-destructive testing. Terminology. Terms used in industrial radiographic testing (1997)
    • EN 1330-4: Non-destructive testing. Terminology. Terms used in ultrasonic testing (2010)
    • EN 1330-7: Non-destructive testing. Terminology. Terms used in magnetic particle testing (2005)
    • EN 1330-8: Non-destructive testing. Terminology. Terms used in leak tightness testing (1998)
    • EN 1330-9: Non-destructive testing. Terminology. Terms used in acoustic emission testing (2009)
    • EN 1330-10: Non-destructive testing. Terminology. Terms used in visual testing (2003)
    • EN 1330-11: Non-destructive testing. Terminology. Terms used in X-ray diffraction from polycrystalline and amorphous materials (2007)
  • ISO 12706: Non-destructive testing. Penetrant testing. Vocabulary (2009)
  • ISO 12718: Non-destructive testing. Eddy current testing. Vocabulary (2008)
Wikimedia Commons has media related to Nondestructive testing.
This article is issued from Wikipedia. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.