Direct reduced iron

Direct-reduced iron (DRI), also called sponge iron,[1] is produced from the direct reduction of iron ore (in the form of lumps, pellets, or fines) to iron by a reducing gas or elementary carbon produced from natural gas or coal. Many ores are suitable for direct reduction.

Reduced iron derives its name from the chemical change that iron ore undergoes when it is heated in a furnace at high temperatures in the presence of hydrocarbon-rich gases, carbon monoxide, or elementary carbon. Direct reduction refers to processes which reduce iron oxides to metallic iron at temperatures below the melting point of iron. The product of such solid state processes is called direct reduced iron.

The reducing gas is a mixture of gases, primarily hydrogen (H2) and carbon monoxide (CO). The process temperature is typically 800 to 1200 °C.[2]

Process

Direct reduction processes can be divided roughly into two categories: gas-based, and coal-based. In both cases, the objective of the process is to drive off the oxygen contained in various forms of iron ore (sized ore, concentrates, pellets, mill scale, furnace dust, etc.), in order to convert the ore to metallic iron, without melting it (below 1200 °C).

The direct reduction process is comparatively energy efficient. Steel made using DRI requires significantly less fuel, in that a traditional blast furnace is not needed. DRI is most commonly made into steel using electric arc furnaces to take advantage of the heat produced by the DRI product.[3]

Benefits

In modern times, direct reduction processes have been developed to specifically overcome the difficulties of conventional blast furnaces. DRI is successfully manufactured in various parts of the world. The initial investment and operating costs of direct reduction plants are low compared to integrated steel plants and are more suitable for developing countries where supplies of coking coal are limited.

Factors that help make DRI economical:

India is the world’s largest producer of direct-reduced iron, a vital constituent of the steel industry.[4] Many other countries use variants of the process, so providing iron for local engineering industries.

Problems

Directly reduced iron is highly susceptible to oxidation and rusting if left unprotected, and is normally quickly processed further to steel. The bulk iron can also catch fire since it is pyrophoric.[5] Unlike blast furnace pig iron, which is almost pure metal, DRI contains some siliceous gangue, which needs to be removed in the steel-making process.

History

Producing sponge iron and then working it was the earliest method used to obtain iron in the Middle East, Egypt, and Europe, where it remained in use until at least the 16th century. There is some evidence that the bloomery method was also used in China, but China had developed blast furnaces to obtain pig iron by 500 BCE.

The advantage of the bloomery technique is that iron can be obtained at a lower furnace temperature, only about 1,100 °C or so. The disadvantage, relative to a blast furnace, is that only small quantities can be made at a time.

Uses

Sponge iron is not useful by itself, but can be processed to create wrought iron. The sponge is removed from the furnace, called a bloomery, and repeatedly beaten with heavy hammers and folded over to remove the slag, oxidise any carbon or carbide and weld the iron together. This treatment usually creates wrought iron with about three percent slag and a fraction of a percent of other impurities. Further treatment may add controlled amounts of carbon, allowing various kinds of heat treatment (e.g. "steeling").

Today, sponge iron is created by reducing iron ore without melting it. This makes for an energy-efficient feedstock for specialty steel manufacturers which used to rely upon scrap metal.

See also

References

Notes
  1. ↑ "What is direct reduced iron (DRI)? definition and meaning". Businessdictionary.com. Retrieved 2011-07-11.
  2. ↑ "Direct reduced iron (DRI)". International Iron Metallics Association.
  3. ↑ R. J. Fruehan, et al. (2000). Theoretical Minimum Energies to Produce Steel (for Selected Conditions)
  4. ↑ "2016 World Direct Reduction Statistics" (PDF). Midrex Technologies. 2016. Retrieved July 7, 2017.
  5. ↑ Hattwig, Martin; Steen, Henrikus (2004), Handbook of explosion prevention and protection, Wiley-VCH, pp. 269–270, ISBN 978-3-527-30718-0.
Bibliography
This article is issued from Wikipedia. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.