Precipitation hardening

Precipitation hardening, also called age hardening or particle hardening, is a heat treatment technique used to increase the yield strength of malleable materials, including most structural alloys of aluminium, magnesium, nickel, titanium, and some steels and stainless steels. In superalloys, it is known to cause yield strength anomaly providing excellent high-temperature strength.

Precipitation hardening relies on changes in solid solubility with temperature to produce fine particles of an impurity phase, which impede the movement of dislocations, or defects in a crystal's lattice. Since dislocations are often the dominant carriers of plasticity, this serves to harden the material. The impurities play the same role as the particle substances in particle-reinforced composite materials. Just as the formation of ice in air can produce clouds, snow, or hail, depending upon the thermal history of a given portion of the atmosphere, precipitation in solids can produce many different sizes of particles, which have radically different properties. Unlike ordinary tempering, alloys must be kept at elevated temperature for hours to allow precipitation to take place. This time delay is called "aging". Solution treatment and aging is sometimes abbreviated "STA" in metals specs and certs.

Note that two different heat treatments involving precipitates can alter the strength of a material: solution heat treating and precipitation heat treating. Solid solution strengthening involves formation of a single-phase solid solution via quenching. Precipitation heat treating involves the addition of impurity particles to increase a material's strength.[1] Precipitation hardening via precipitation heat treatment is the main topic of discussion in this article.

Kinetics versus thermodynamics

This technique exploits the phenomenon of supersaturation, and involves careful balancing of the driving force for precipitation and the thermal activation energy available for both desirable and undesirable processes.

Nucleation occurs at a relatively high temperature (often just below the solubility limit) so that the kinetic barrier of surface energy can be more easily overcome and the maximum number of precipitate particles can form. These particles are then allowed to grow at lower temperature in a process called aging. This is carried out under conditions of low solubility so that thermodynamics drive a greater total volume of precipitate formation.

Diffusion's exponential dependence upon temperature makes precipitation strengthening, like all heat treatments, a fairly delicate process. Too little diffusion (under aging), and the particles will be too small to impede dislocations effectively; too much (over aging), and they will be too large and dispersed to interact with the majority of dislocations.

Alloy design

Precipitation strengthening is possible if the line of solid solubility slopes strongly toward the center of a phase diagram. While a large volume of precipitate particles is desirable, a small enough amount of the alloying element should be added that it remains easily soluble at some reasonable annealing temperature.

Elements used for precipitation strengthening in typical aluminum and titanium alloys make up about 10% of their composition. While binary alloys are more easily understood as an academic exercise, commercial alloys often use three components for precipitation strengthening, in compositions such as Al(Mg, Cu) and Ti(Al, V). A large number of other constituents may be unintentional, but benign, or may be added for other purposes such as grain refinement or corrosion resistance. In some cases, such as many aluminum alloys, an increase in strength is achieved at the expense of corrosion resistance.

The addition of large amounts of nickel and chromium needed for corrosion resistance in stainless steels means that traditional hardening and tempering methods are not effective. However, precipitates of chromium, copper, or other elements can strengthen the steel by similar amounts in comparison to hardening and tempering. The strength can be tailored by adjusting the annealing process, with lower initial temperatures resulting in higher strengths. The lower initial temperatures increase the driving force of nucleation. More driving force means more nucleation sites, and more sites means more places for dislocations to be disrupted while the finished part is in use.

Many alloy systems allow the aging temperature to be adjusted. For instance, some aluminium alloys used to make rivets for aircraft construction are kept in dry ice from their initial heat treatment until they are installed in the structure. After this type of rivet is deformed into its final shape, aging occurs at room temperature and increases its strength, locking the structure together. Higher aging temperatures would risk over-aging other parts of the structure, and require expensive post-assembly heat treatment. Too high of an aging temperature promotes the precipitate to grow too readily.

Types of hardening

There are a number of ways by which a matrix can be hardened by precipitates.[2]

1. Coherency hardening

2. Modulus hardening

3. Chemical hardening

4. Order strengthening

Theory

The primary species of precipitation strengthening are second phase particles. These particles impede the movement of dislocations throughout the lattice. You can determine whether or not second phase particles will precipitate into solution from the solidus line on the phase diagram for the particles. Physically, this strengthening effect can be attributed both to size and modulus effects, and to interfacial or surface energy.

The presence of second phase particles often causes lattice distortions. These lattice distortions result when the precipitate particles differ in size and crystallographic structure from the host atoms. Smaller precipitate particles in a host lattice leads to a tensile stress, whereas larger precipitate particles leads to a compressive stress. Dislocation defects also create a stress field. Above the dislocation there is a compressive stress and below there is a tensile stress. Consequently, there is a negative interaction energy between a dislocation and a precipitate that each respectively cause a compressive and a tensile stress or vice versa. In other words, the dislocation will be attracted to the precipitate. In addition, there is a positive interaction energy between a dislocation and a precipitate that have the same type of stress field. This means that the dislocation will be repulsed by the precipitate.

Precipitate particles also serve by locally changing the stiffness of a material. Dislocations are repulsed by regions of higher stiffness. Conversely, if the precipitate causes the material to be locally more compliant, then the dislocation will be attracted to that region. In addition, there are three types of interphase boundaries (IPBs), shown in Figure 1.

In (a), it is a coherent or ordered IPB, the atoms match up one by one along the boundary. Due to difference in lattice parameters of the two phases, a coherency strain energy is associated with this type of boundary. In (b), it is a fully disordered IPB and there are no coherency strains. In (c), it is a partially ordered IPB, so coherency strains are partially relieved by the periodic introduction of dislocations along the boundary.

Here is a schematic of a coherent precipitate in a matrix, shown in Figure 2. The precipitate has a lattice parameter less than that of the matrix, the atomic match across the IPB leads to an internal stress field that interacts with moving dislocations. 

There are two deformation paths, one is the coherency hardening, the lattice mismatch is

Where G is the shear modulus, is the coherent lattice mismatch, r is the particle radius, f is the particle volume fraction, b is the burgers vector,  rf/b equals the concentration. The other one is modulus hardening, a schematic is shown in Figure 3. 

The energy of the dislocation energy is , when it cuts through the precipitate, its energy is , the change in line segment energy is

.

The maximum dislocation length affected is the particle diameter, the line tension change takes place gradually over a distance equal to r. The interaction force between the dislocation and the precipitate is

and .

Furthermore, a dislocation may cut through a precipitate particle. A schematic of this process is shown in Figure 4. In (a), the dislocation is approaching the particle, in (b), it is within the particle and an offset, b, of a portion of the upper part of the particle with respect to the lower part accompanies the dislocation entry. In (c), a similar offset is effected when the dislocation exits the particle. The complete transit is accompanied by creation of matrix-precipitate surface area of approximate magnitude , where r is the radius of the particle and b is the magnitude of the burgers vector. The resulting increase in surface energy is , where is the surface energy. The maximum force between the dislocation and particle is , the corresponding flow stress should be .

When a particle is sheared by a dislocation, a threshold shear stress is needed to deform the particle. A schematic of the stress required for dislocations to shear precipitates as a function of precipitate size is shown in Figure 5. The expression for the required shear stress is as follows:

When the precipitate size is small, the required shear stress is proportional to the precipitate size , However, for a fixed particle volume fraction, this stress may decrease at larger values of r owing to an increase in particle spacing. The overall level of the curve is raised by increases in either inherent particle strength or particle volume fraction. 

The dislocation can also bow around a precipitate particle through so-called Orowan mechanism. A schematic of a dislocation approach nondeforming particles is shown in Figure 6.

Since the particle is nondeforming, the dislocation bows around the particles (), the stress required to effect the bypassing is inversely proportional to the interparticle spacing (L-2r), that is, , where r is the particle radius. Dislocation loops encircle the particles after the bypass operation, a subsequent dislocation would have to be extruded between the loops. Thus, the effective particle spacing for the second dislocation is reduced to (L-2r`) with r`>r, and the bypassing stress for this dislocation should be , which is greater than for the first one. However, as the radius of particle increases, L will increase so as to maintain the same volume fraction of precipitates, (L-2r) will increase and will decrease. As a result, the material will become weaker as the precipitate size increases.

Figure 7 shows the bowing stress and particle size relationship. On one hand, for a fixed particle volume fraction,  decreases with increasing r as this is accompanied by an increase in particle spacing.

On the other hand, increasing f increases the level of the stress as a result of a finer particle spacing. The level of is unaffected by particle strength. That is, once a particle is strong enough to resist cutting, any further increase in its resistance to dislocation penetration has no effect on , which depends only on matrix properties and effective particle spacing.

If particles of A of volume fraction are dispersed in a matrix, particles are sheared for and are bypassed for , maximum strength is obtained at , where the cutting and bowing stresses are equal. If inherently harder particles of B of the same volume fraction are present, the level of the curve is increased but that of the one is not. Maximum hardening, greater than that for A particles, is found at . Increasing the volume fraction of A raises the level of both and and increases the maximum strength obtained. The latter is found at , which may be either less than or greater than depending on the shape of the curve.

Governing equations

There are two equations to describe the two mechanisms for precipitation hardening:

Dislocations cutting through particles:

where is material strength, is the second phase particle radius, is the surface energy, is the magnitude of the Burgers vector, and is the spacing between pinning points. This governing equation shows that the strength is proportional to , the radius of the precipitate particles. This means that it is easier for dislocations to cut through a material with smaller second phase particles (small r). As the size of the second phase particles increases, the particles impede dislocation movement and it becomes increasingly difficult for the particles to cut through the material. In other words, the strength of a material increases with increasing r.

Dislocations bowing around particle:Precipitation hardening, also called age hardening or particle hardening, is a heat treatment technique used to increase the yield strength of malleable materials, including most structural alloys of aluminium, magnesium, nickel, titanium, and some steels and stainless steels. In superalloys, it is known to cause yield strength anomaly providing excellent high-temperature strength.

where is the material strength, is the shear modulus, is the magnitude of the Burgers vector, is the distance between pinning points, and is the second phase particle radius. This governing equation shows that for dislocation bowing the strength is inversely proportional to the second phase particle radius r. Dislocation bowing, also called Orowan strengthening,[3] is more likely to occur when the particle density in the material is lower.

These governing equations show that the precipitation hardening mechanism depends on the size of the precipitate particles. At small r, cutting will dominate, while at large r, bowing will dominate.

Looking at the plot of both equations, it is clear that there is a critical radius at which max strengthening occurs. This critical radius is typically 5-30 nm.

Examples of precipitation hardening materials

See also

References

  1. W.D. Callister. Fundamentals of Materials Science and Engineering, 2nd ed. Wiley & Sons. pp. 252.
  2. Thosmas H. Courtney. Mechanical Behavior of Materials, 2nd ed. Waveland Press, Inc.. pp. 198-205.
  3. Orowan Bowing

Further reading