Titanium diboride

Titanium diboride

Identifiers
CAS Number	12045-63-5 Y
Properties
Chemical formula	TiB2
Molar mass	69.489 g/mol
Appearance	non lustrous metallic grey
Density	4.52 g/cm3
Melting point	3,230 °C (5,850 °F; 3,500 K)
Structure
Crystal structure	Hexagonal, Space group P6/mmm. Lattice parameters at room temperature: a=302.36 pm, C=322.04 pm
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
Y verify (what is YN ?)
Infobox references

Titanium diboride (TiB₂) is an extremely hard ceramic which has excellent heat conductivity, oxidation stability and resistance to mechanical erosion. TiB₂ is also a reasonable electrical conductor,^[1] so it can be used as a cathode material in aluminium smelting and can be shaped by electrical discharge machining.

Physical properties

TiB₂ is very similar to titanium carbide, an important base material for cermets, and many of its properties (e.g. hardness, thermal conductivity, electrical conductivity and oxidation resistance) are superior to those of TiC:^[2]

• Exceptional hardness (25–35 GPa Vickers at room temperature, more than three times harder than fully hardened structural steel), which is retained up to high temperature.
• High melting point (3225 °C),
• High thermal conductivity (60-120 W/(m K)),
• High electrical conductivity (~10⁵ S/cm)

Chemical properties

With respect to chemical stability, TiB₂ is more stable in contact with pure iron than tungsten carbide or silicon nitride.^[2]

TiB₂ is resistant to oxidation in air at temperatures up to 1100 °C,^[2] and to hydrochloric and hydrofluoric acids, but reacts with alkalis, nitric acid and sulfuric acid.

Production

TiB₂ does not occur naturally in the earth. Titanium diboride powder can be prepared by a variety of high-temperature methods, such as the direct reactions of titanium or its oxides/hydrides, with elemental boron over 1000 °C, carbothermal reduction by thermite reaction of titanium oxide and boron oxide, or hydrogen reduction of boron halides in the presence of the metal or its halides. Among various synthesis routes, electrochemical synthesis and solid state reactions have been developed to prepare finer titanium diboride in large quantity. An example of solid state reaction is the borothermic reduction, which can be illustrated by the following reaction

2 TiO₂ + B₄C + 3C → 2 TiB₂ + 4 CO

These synthesis routes, however, cannot produce nanosized powders. Nanocrystalline (5–100 nm) TiB₂ was synthesized using the following techniques:

• Solution phase reaction of NaBH₄ and TiCl₄, followed by annealing the amorphous precursor obtained at 900–1100 °C.^[3]
• Mechanical alloying of a mixture of elemental Ti and B powders.^[4]
• Self-propagating high temperature synthesis process involving addition of varying amounts of NaCl.^[5]
• Solvothermal reaction in benzene of metallic sodium with amorphous boron powder and TiCl₄ at 400 °C:^[6]

TiCl₄ + 2 B + 4 Na → TiB₂ + 4 NaCl

Many TiB₂ applications are inhibited by economic factors, particularly the costs of densifying a high melting point material - the melting point is about 2970 °C, and, thanks to a layer of titanium dioxide that forms on the surface of the particles of a powder, it is very resistant to sintering. Admixture of about 10% silicon nitride facilitates the sintering,^[7] though sintering without silicon nitride has been demonstrated as well.^[1]

Thin films of TiB₂ can be produced by several techniques. The electroplating of TiB₂ layers possess two main advantages compared with physical vapor deposition or chemical vapor deposition: the growing rate of the layer is 200 times higher (up to 5 μm/s) and the inconveniences of covering complex shaped products are dramatically reduced.

Potential applications

Current use of TiB₂ appears to be limited to specialized applications in such areas as impact resistant armor, cutting tools, crucibles, neutron absorbers and wear resistant coatings.

TiB₂ is extensively used as evaporation boats for vapour coating of aluminium. It is an attractive material for the aluminium industry as an inoculant to refine the grain size when casting aluminium alloys, because of its wettability by and low solubility in molten aluminium and good electrical conductivity.

Thin films of TiB₂ can be used to provide wear and corrosion resistance to a cheap and/or tough substrate.