Quasicrystal

Not to be confused with Quasi-crystals (supramolecular).
Potential energy surface for silver depositing on an aluminium-palladium-manganese (Al-Pd-Mn) quasicrystal surface. Similar to Fig. 6 in Ref.[1]

A quasiperiodic crystal, or quasicrystal, is a structure that is ordered but not periodic. A quasicrystalline pattern can continuously fill all available space, but it lacks translational symmetry. While crystals, according to the classical crystallographic restriction theorem, can possess only two, three, four, and six-fold rotational symmetries, the Bragg diffraction pattern of quasicrystals shows sharp peaks with other symmetry orders, for instance five-fold.

Aperiodic tilings were discovered by mathematicians in the early 1960s, and, some twenty years later, they were found to apply to the study of quasicrystals. The discovery of these aperiodic forms in nature has produced a paradigm shift in the fields of crystallography. Quasicrystals had been investigated and observed earlier,[2] but, until the 1980s, they were disregarded in favor of the prevailing views about the atomic structure of matter. In 2009, after a dedicated search, a mineralogical finding, icosahedrite, offered evidence for the existence of natural quasicrystals.[3]

Roughly, an ordering is non-periodic if it lacks translational symmetry, which means that a shifted copy will never match exactly with its original. The more precise mathematical definition is that there is never translational symmetry in more than n – 1 linearly independent directions, where n is the dimension of the space filled, e.g., the three-dimensional tiling displayed in a quasicrystal may have translational symmetry in two dimensions. The ability to diffract comes from the existence of an indefinitely large number of elements with a regular spacing, a property loosely described as long-range order. Experimentally, the aperiodicity is revealed in the unusual symmetry of the diffraction pattern, that is, symmetry of orders other than two, three, four, or six. In 1982 materials scientist Dan Shechtman observed that certain aluminium-manganese alloys produced the unusual diffractograms which today are seen as revelatory of quasicrystal structures. Due to fear of the scientific community's reaction, it took him two years to publish the results[4][5] for which he was awarded the Nobel Prize in Chemistry in 2011.[6]

History

A Penrose tiling

In 1961, Hao Wang asked whether determining if a set of tiles admits a tiling of the plane is an algorithmically unsolvable problem or not. He conjectured that it is solvable, relying on the hypothesis that every set of tiles that can tile the plane can do it periodically (hence, it would suffice to try to tile bigger and bigger patterns until obtaining one that tiles periodically). Nevertheless, two years later, his student Robert Berger constructed a set of some 20,000 square tiles (now called Wang tiles) that can tile the plane but not in a periodic fashion. As further aperiodic sets of tiles were discovered, sets with fewer and fewer shapes were found. in 1976 Roger Penrose discovered a set of just two tiles, now referred to as Penrose tiles, that produced only non-periodic tilings of the plane. These tilings displayed instances of fivefold symmetry. One year later Alan Mackay showed experimentally that the diffraction pattern from the Penrose tiling had a two-dimensional Fourier transform consisting of sharp 'delta' peaks arranged in a fivefold symmetric pattern.[7] Around the same time Robert Ammann created a set of aperiodic tiles that produced eightfold symmetry.

Mathematically, quasicrystals have been shown to be derivable from a general method that treats them as projections of a higher-dimensional lattice. Just as circles, ellipses, and hyperbolic curves in the plane can be obtained as sections from a three-dimensional double cone, so too various (aperiodic or periodic) arrangements in two and three dimensions can be obtained from postulated hyperlattices with four or more dimensions. Icosahedral quasicrystals in three dimensions were projected from a six-dimensional hypercubic lattice by Peter Kramer and Roberto Neri in 1984.[8] The tiling is formed by two tiles with rhombohedral shape.

Shechtman first observed ten-fold electron diffraction patterns in 1982, as described in his notebook. The observation was made during a routine investigation, by electron microscopy, of a rapidly cooled alloy of aluminium and manganese prepared at the US National Bureau of Standards (later NIST).

In the summer of the same year Shechtman visited Ilan Blech and related his observation to him. Blech responded that such diffractions had been seen before.[9][10] Around that time, Shechtman also related his finding to John Cahn of NIST who did not offer any explanation and challenged him to solve the observation. Shechtman quoted Cahn as saying: "Danny, this material is telling us something and I challenge you to find out what it is".

The observation of the ten-fold diffraction pattern lay unexplained for two years until the spring of 1984, when Blech asked Shechtman to show him his results again. A quick study of Shechtman's results showed that the common explanation for a ten-fold symmetrical diffraction pattern, the existence of twins, was ruled out by his experiments. Since periodicity and twins were ruled out, Blech, unaware of the two-dimensional tiling work, was looking for another possibility: a completely new structure containing cells connected to each other by defined angles and distances but without translational periodicity. Blech decided to use a computer simulation to calculate the diffraction intensity from a cluster of such a material without long-range translational order but still not random. He termed this new structure multiple polyhedral.

The idea of a new structure was the necessary paradigm shift to break the impasse. The “Eureka moment” came when the computer simulation showed sharp ten-fold diffraction patterns, similar to the observed ones, emanating from the three-dimensional structure devoid of periodicity. The multiple polyhedral structure was termed later by many researchers as icosahedral glass but in effect it embraces any arrangement of polyhedra connected with definite angles and distances (this general definition includes tiling, for example).

Shechtman accepted Blech's discovery of a new type of material and it gave him the courage to publish his experimental observation. Shechtman and Blech jointly wrote a paper entitled "The Microstructure of Rapidly Solidified Al6Mn" [11] and sent it for publication around June 1984 to the Journal of Applied Physics (JAP). The JAP editor promptly rejected the paper as being better fit for a metallurgical readership. As a result, the same paper was re-submitted for publication to the Metallurgical Transactions A, where it was accepted. Although not noted in the body of the published text, the published paper was slightly revised prior to publication.

Meanwhile, on seeing the draft of the Shechtman-Blech paper in the summer of 1984, John Cahn suggested that Shechtman's experimental results merit a fast publication in a more appropriate scientific journal. Shechtman agreed and, in hindsight, called this fast publication "a winning move”. This paper, published in the Physical Review Letters (PRL),[5] repeated Shechtman's observation and used the same illustrations as the original Shechtman-Blech paper in the Metallurgical Transactions A. The PRL paper, the first to appear in print, caused considerable excitement in the scientific community.

Next year Ishimasa et al. reported twelvefold symmetry in Ni-Cr particles.[12] Soon, eightfold diffraction patterns were recorded in V-Ni-Si and Cr-Ni-Si alloys.[13] Over the years, hundreds of quasicrystals with various compositions and different symmetries have been discovered. The first quasicrystalline materials were thermodynamically unstable—when heated, they formed regular crystals. However, in 1987, the first of many stable quasicrystals were discovered, making it possible to produce large samples for study and opening the door to potential applications. In 2009, following a 10-year systematic search, scientists reported the first natural quasicrystal, a mineral found in the Khatyrka River in eastern Russia.[3] This natural quasicrystal exhibits high crystalline quality, equalling the best artificial examples.[14] The natural quasicrystal phase, with a composition of Al63Cu24Fe13, was named icosahedrite and it was approved by the International Mineralogical Association in 2010. Furthermore, analysis indicates it may be meteoritic in origin, possibly delivered from a carbonaceous chondrite asteroid.[15]

Atomic image of a micron-sized grain of the natural Al71Ni24Fe5 quasicrystal (shown in the inset) from a Khatyrka meteorite. The corresponding diffraction patterns reveal a ten-fold symmetry.[16]

A further study of Khatyrka meteorites revealed micron-sized grains of another natural quasicrystal, which has a ten-fold symmetry and a chemical formula of Al71Ni24Fe5. This quasicrystal is stable in a narrow temperature range, from 1120 to 1200 K at ambient pressure, which suggests that natural quasicrystals are formed by rapid quenching of a meteorite heated during an impact-induced shock.[16]

Electron diffraction pattern of an icosahedral Ho-Mg-Zn quasicrystal

In 1972 de Wolf and van Aalst[17] reported that the diffraction pattern produced by a crystal of sodium carbonate cannot be labeled with three indices but needed one more, which implied that the underlying structure had four dimensions in reciprocal space. Other puzzling cases have been reported,[18] but until the concept of quasicrystal came to be established, they were explained away or denied.[19][20] However, at the end of the 1980s the idea became acceptable, and in 1992 the International Union of Crystallography altered its definition of a crystal, broadening it as a result of Shechtman’s findings, reducing it to the ability to produce a clear-cut diffraction pattern and acknowledging the possibility of the ordering to be either periodic or aperiodic.[4][notes 1] Now, the symmetries compatible with translations are defined as "crystallographic", leaving room for other "non-crystallographic" symmetries. Therefore, aperiodic or quasiperiodic structures can be divided into two main classes: those with crystallographic point-group symmetry, to which the incommensurately modulated structures and composite structures belong, and those with non-crystallographic point-group symmetry, to which quasicrystal structures belong.

Originally, the new form of matter was dubbed "Shechtmanite".[21] The term "quasicrystal" was first used in print by Steinhardt and Levine[22] shortly after Shechtman's paper was published. The adjective quasicrystalline had already been in use, but now it came to be applied to any pattern with unusual symmetry.[notes 2] 'Quasiperiodical' structures were claimed to be observed in some decorative tilings devised by medieval Islamic architects.[23][24] For example, Girih tiles in a medieval Islamic mosque in Isfahan, Iran, are arranged in a two-dimensional quasicrystalline pattern.[25] These claims have, however, been under some debate.[26]

Shechtman was awarded the Nobel Prize in Chemistry in 2011 for his work on quasicrystals. "His discovery of quasicrystals revealed a new principle for packing of atoms and molecules," stated the Nobel Committee and pointed that "this led to a paradigm shift within chemistry." [4][27]

Mathematics

A penteract (5-cube) pattern using 5D orthographic projection to 2D using Petrie polygon basis vectors overlaid on the diffractogram from an Icosahedral Ho-Mg-Zn quasicrystal
A hexeract (6-cube) pattern using 6D orthographic projection to a 3D Perspective (visual) object (the Rhombic triacontahedron) using the Golden ratio in the basis vectors. This is used to understand the aperiodic Icosahedral structure of Quasicrystals.

There are several ways to mathematically define quasicrystalline patterns. One definition, the "cut and project" construction, is based on the work of Harald Bohr (mathematician brother of Niels Bohr). The concept of an almost periodic function (also called a quasiperiodic function) was studied by Bohr, including work of Bohl and Escanglon.[28] He introduced the notion of a superspace. Bohr showed that quasiperiodic functions arise as restrictions of high-dimensional periodic functions to an irrational slice (an intersection with one or more hyperplanes), and discussed their Fourier point spectrum. These functions are not exactly periodic, but they are arbitrarily close in some sense, as well as being a projection of an exactly periodic function.

In order that the quasicrystal itself be aperiodic, this slice must avoid any lattice plane of the higher-dimensional lattice. De Bruijn showed that Penrose tilings can be viewed as two-dimensional slices of five-dimensional hypercubic structures.[29] Equivalently, the Fourier transform of such a quasicrystal is nonzero only at a dense set of points spanned by integer multiples of a finite set of basis vectors (the projections of the primitive reciprocal lattice vectors of the higher-dimensional lattice).[30] The intuitive considerations obtained from simple model aperiodic tilings are formally expressed in the concepts of Meyer and Delone sets. The mathematical counterpart of physical diffraction is the Fourier transform and the qualitative description of a diffraction picture as 'clear cut' or 'sharp' means that singularities are present in the Fourier spectrum. There are different methods to construct model quasicrystals. These are the same methods that produce aperiodic tilings with the additional constraint for the diffractive property. Thus, for a substitution tiling the eigenvalues of the substitution matrix should be Pisot numbers. The aperiodic structures obtained by the cut-and-project method are made diffractive by choosing a suitable orientation for the construction; this is a geometric approach that has also a great appeal for physicists.

Classical theory of crystals reduces crystals to point lattices where each point is the center of mass of one of the identical units of the crystal. The structure of crystals can be analyzed by defining an associated group. Quasicrystals, on the other hand, are composed of more than one type of unit, so, instead of lattices, quasilattices must be used. Instead of groups, groupoids, the mathematical generalization of groups in category theory, is the appropriate tool for studying quasicrystals.[31]

Using mathematics for construction and analysis of quasicrystal structures is a difficult task for most experimentalists. Computer modeling, based on the existing theories of quasicrystals, however, greatly facilitated this task. Advanced programs have been developed[32] allowing one to construct, visualize and analyze quasicrystal structures and their diffraction patterns.

Interacting spins were also analyzed in quasicrystals: AKLT Model and 8-vertex model were solved in quasicrystals analytically [33]

Materials science

Tiling of a plane by regular pentagons is impossible but can be realized on a sphere in the form of pentagonal dodecahedron.
A Ho-Mg-Zn icosahedral quasicrystal formed as a pentagonal dodecahedron, the dual of the icosahedron. Unlike the similar pyritohedron shape of some cubic-system crystals such as pyrite, the quasicrystal has faces that are true regular pentagons
TiMn quasicrystal approximant lattice.

Since the original discovery by Dan Shechtman, hundreds of quasicrystals have been reported and confirmed. Undoubtedly, the quasicrystals are no longer a unique form of solid; they exist universally in many metallic alloys and some polymers. Quasicrystals are found most often in aluminium alloys (Al-Li-Cu, Al-Mn-Si, Al-Ni-Co, Al-Pd-Mn, Al-Cu-Fe, Al-Cu-V, etc.), but numerous other compositions are also known (Cd-Yb, Ti-Zr-Ni, Zn-Mg-Ho, Zn-Mg-Sc, In-Ag-Yb, Pd-U-Si, etc.).[34]

Two types of quasicrystals are known.[32] The first type, polygonal (dihedral) quasicrystals, have an axis of 8, 10, or 12-fold local symmetry (octagonal, decagonal, or dodecagonal quasicrystals, respectively). They are periodic along this axis and quasiperiodic in planes normal to it. The second type, icosahedral quasicrystals, are aperiodic in all directions.

Quasicrystals fall into three groups of different thermal stability:[35]

Except for the Al–Li–Cu system, all the stable quasicrystals are almost free of defects and disorder, as evidenced by X-ray and electron diffraction revealing peak widths as sharp as those of perfect crystals such as Si. Diffraction patterns exhibit fivefold, threefold, and twofold symmetries, and reflections are arranged quasiperiodically in three dimensions.

The origin of the stabilization mechanism is different for the stable and metastable quasicrystals. Nevertheless, there is a common feature observed in most quasicrystal-forming liquid alloys or their undercooled liquids: a local icosahedral order. The icosahedral order is in equilibrium in the liquid state for the stable quasicrystals, whereas the icosahedral order prevails in the undercooled liquid state for the metastable quasicrystals.

A nanoscale icosahedral phase was formed in Zr-, Cu- and Hf-based bulk metallic glasses alloyed with noble metals.[36]

Most quasicrystals have ceramic-like properties including high thermal and electrical resistance, hardness and brittleness, resistance to corrosion, and non-stick properties.[37] Many metallic quasicrystalline substances are impractical for most applications due to their thermal instability; the Al-Cu-Fe ternary system and the Al-Cu-Fe-Cr and Al-Co-Fe-Cr quaternary systems, thermally stable up to 700 °C, are notable exceptions.

Applications

Quasicrystalline substances have potential applications in several forms. The tendency to brittleness is a problem that must be overcome.

Quasicrystalline coatings benefit from hardness while avoiding the brittleness in bulk material.

Another way to get round the brittleness of quasicrystalline bulk material is the utilization of an Al-based alloy (typically Al-Mn-Ce) reinforced by precipitation of icosahedral particles in the nanometer range. Such materials are commercially available, and can be very strong but much lighter than material with comparable properties. This may be particularly relevant to the aviation industry, where strength and low weight are both of greet importance.[38]

A third potential speculated application is as a reversible storage medium for hydrogen. Storage capabilities of almost two hydrogen atoms per metal atom have been reported for Zr-based quasicrystals, comparable to the storage capability of Ti-Fe hybrids.[38]

Metallic quasicrystalline coatings can be applied by plasma-coating or magnetron sputtering. A problem that must be resolved is the tendency for cracking due to the materials' extreme brittleness.[37]

An application was the use of low-friction Al-Cu-Fe-Cr quasicrystals[39] as a coating for frying pans. Food did not stick to it as much as to stainless steel making the pan moderately non-stick and easy to clean; heat transfer and durability were better than PTFE non-stick cookware and the pan was free from perfluorooctanoic acid (PFOA); the surface was very hard, claimed to be ten times harder than stainless steel, and not harmed by metal utensils or cleaning in a dishwasher; and the pan could withstand temperatures of 1,000 °C (1,800 °F) without harm.[40] However, cooking with a lot of salt would etch the quasicrystalline coating used, and the pans were eventually withdrawn from production. Shechtman had one of these pans.[41]

The Nobel citation said that quasicrystals, while brittle, could reinforce steel "like armor". When Shechtman was asked about potential applications of quasicrstals he said that a precipitation-hardened stainless steel is produced that is strengthened by small quasicrystalline particles. It does not corrode and is extremely strong, suitable for razor blades and surgery instruments. The small quasicrystalline particles impede the motion of dislocation in the material.[41]

Quasicrystals were also being used to develop heat insulation, LEDs, diesel engines, and new materials that convert heat to electricity. Shechtman suggested new applications taking advantage of the low coefficient of friction and the hardness of some quasicrystalline materials, for example embedding particles in plastic to make strong, hard-wearing, low-friction plastic gears. The low heat conductivity of some quasicrystals makes them good for heat insulating coatings.[41]

Other potential applications include selective solar absorbers for power conversion, broad-wavelength reflectors, and bone repair and prostheses applications where biocompatibility, low friction and corrosion resistance are required. Magnetron sputtering can be readily applied to other stable quasicrystalline alloys such as Al-Pd-Mn.[37]

While saying that the discovery of icosahedrite, the first quasicrystal found in nature, was important, Shechtman saw no practical applications.

See also

Notes

  1. ↑ The concept of aperiodic crystal was coined by Erwin Schrödinger in another context with a somewhat different meaning. In his popular book What is life? in 1944, Schrödinger sought to explain how hereditary information is stored: molecules were deemed too small, amorphous solids were plainly chaotic, so it had to be a kind of crystal; as a periodic structure could encode very little information, it had to be aperiodic. DNA was later discovered, and, although not crystalline, it possesses properties predicted by Schrödinger—it is a regular but aperiodic molecule.
  2. ↑ The use of the adjective 'quasicrystalline' for qualifying a structure can be traced back to the mid-1940-50s, e.g. in Kratky, O; Porod, G (1949). "Diffuse small-angle scattering of x-rays in colloid systems". Journal of Colloid Science 4 (1): 35–70. doi:10.1016/0095-8522(49)90032-X. PMID 18110601.; Gunn, R (1955). "The statistical electrification of aerosols by ionic diffusion". Journal of Colloid Science 10: 107–119. doi:10.1016/0095-8522(55)90081-7.

References

  1. ↑ Ünal, B; V. Fournée; K.J. Schnitzenbaumer; C. Ghosh; C.J. Jenks; A.R. Ross; T.A. Lograsso; J.W. Evans; P.A. Thiel (2007). "Nucleation and growth of Ag islands on fivefold Al-Pd-Mn quasicrystal surfaces: Dependence of island density on temperature and flux". Physical Review B 75 (6): 064205. Bibcode:2007PhRvB..75f4205U. doi:10.1103/PhysRevB.75.064205.
  2. ↑ Steurer W. (2004). "Twenty years of structure research on quasicrystals. Part I. Pentagonal, octagonal, decagonal and dodecagonal quasicrystals". Z. Kristallogr. 219 (7–2004): 391–446. Bibcode:2004ZK....219..391S. doi:10.1524/zkri.219.7.391.35643.
  3. 1 2 Bindi, L.; Steinhardt, P. J.; Yao, N.; Lu, P. J. (2009). "Natural Quasicrystals". Science 324 (5932): 1306–9. Bibcode:2009Sci...324.1306B. doi:10.1126/science.1170827. PMID 19498165.
  4. 1 2 3 Andrea Gerlin (5 October 2011). "Technion’s Shechtman Wins Nobel in Chemistry for Quasicrystals Discovery". Bloomberg.
  5. 1 2 Shechtman, D.; Blech, I.; Gratias, D.; Cahn, J. (1984). "Metallic Phase with Long-Range Orientational Order and No Translational Symmetry". Physical Review Letters 53 (20): 1951–1953. Bibcode:1984PhRvL..53.1951S. doi:10.1103/PhysRevLett.53.1951.
  6. ↑ "The Nobel Prize in Chemistry 2011". Nobelprize.org. Retrieved 2011-10-06.
  7. ↑ Mackay, A.L. (1982). "Crystallography and the Penrose Pattern". Physica A 114: 609–613. Bibcode:1982PhyA..114..609M. doi:10.1016/0378-4371(82)90359-4.
  8. ↑ Kramer, P.; Neri, R. (1984). "On periodic and non-periodic space fillings of Em obtained by projection". Acta Crystallographica A 40 (5): 580–587. doi:10.1107/S0108767384001203.
  9. ↑ Yang, C. Y. (1979). "Crystallography of decahedral and icosahedral particles". J. Cryst. Growth 47 (2): 274–282. Bibcode:1979JCrGr..47..274Y. doi:10.1016/0022-0248(79)90252-5.
  10. ↑ Yang, C. Y.; Yacaman, M. J.; Heinemann, K. (1979). "Crystallography of decahedral and icosahedral particles". J. Cryst. Growth 47 (2): 283–290. Bibcode:1979JCrGr..47..283Y. doi:10.1016/0022-0248(79)90253-7.
  11. ↑ Shechtman, Dan; I. A. Blech (1985). "The Microstructure of Rapidly Solidified Al6Mn". Met. Trans. A 16A (6): 1005–1012. Bibcode:1985MTA....16.1005S. doi:10.1007/BF02811670.
  12. ↑ Ishimasa, T.; Nissen, H.-U.; Fukano, Y. (1985). "New ordered state between crystalline and amorphous in Ni-Cr particles". Physical Review Letters 55 (5): 511–513. Bibcode:1985PhRvL..55..511I. doi:10.1103/PhysRevLett.55.511. PMID 10032372.
  13. ↑ Wang, N.; Chen, H.; Kuo, K. (1987). "Two-dimensional quasicrystal with eightfold rotational symmetry". Physical Review Letters 59 (9): 1010–1013. Bibcode:1987PhRvL..59.1010W. doi:10.1103/PhysRevLett.59.1010. PMID 10035936.
  14. ↑ Steinhardt, Paul; Bindi, Luca (2010). "Once upon a time in Kamchatka: the search for natural quasicrystals". Philosophical Magazine 91 (19–21): 1. Bibcode:2011PMag...91.2421S. doi:10.1080/14786435.2010.510457.
  15. ↑ Bindi, Luca; John M. Eiler; Yunbin Guan; Lincoln S. Hollister; Glenn MacPherson; Paul J. Steinhardt; Nan Yao (2012-01-03). "Evidence for the extraterrestrial origin of a natural quasicrystal". Proceedings of the National Academy of Sciences 109 (5): 1396–1401. Bibcode:2012PNAS..109.1396B. doi:10.1073/pnas.1111115109. Retrieved 2012-01-04.
  16. 1 2 Bindi, L.; Yao, N.; Lin, C.; Hollister, L. S.; Andronicos, C. L.; Distler, V. V.; Eddy, M. P.; Kostin, A.; Kryachko, V.; MacPherson, G. J.; Steinhardt, W. M.; Yudovskaya, M.; Steinhardt, P. J. (2015). "Natural quasicrystal with decagonal symmetry". Scientific Reports 5: 9111. Bibcode:2015NatSR...5E9111B. doi:10.1038/srep09111. PMC 4357871. PMID 25765857.
  17. ↑ de Wolf, R.M. and van Aalst, W. (1972). "The four dimensional group of γ-Na2CO3". Acta Crystallogr. A 28: S111.
  18. ↑ Kleinert H. and Maki K. (1981). "Lattice Textures in Cholesteric Liquid Crystals" (PDF). Fortschritte der Physik 29 (5): 219–259. Bibcode:1981ForPh..29..219K. doi:10.1002/prop.19810290503.
  19. ↑ Pauling, L (1987-01-26). "So-called icosahedral and decagonal quasicrystals are twins of an 820-atom cubic crystal. Pauling L". Physical Review Letters 58 (4): 365–368. Bibcode:1987PhRvL..58..365P. doi:10.1103/PhysRevLett.58.365. PMID 10034915.
  20. ↑ Kenneth Chang (October 5, 2011). "Israeli Scientist Wins Nobel Prize for Chemistry". NY Times.
  21. ↑ Browne, Malcolm W. (1989-09-05). "Impossible' Form of Matter Takes Spotlight In Study of Solids". New York Times.
  22. ↑ Levine, Dov; Steinhardt, Paul (1984). "Quasicrystals: A New Class of Ordered Structures". Physical Review Letters 53 (26): 2477–2480. Bibcode:1984PhRvL..53.2477L. doi:10.1103/PhysRevLett.53.2477.
  23. ↑ Makovicky, E. (1992), 800-year-old pentagonal tiling from Maragha, Iran, and the new varieties of aperiodic tiling it inspired. In: I. Hargittai, editor: Fivefold Symmetry, pp. 67–86. World Scientific, Singapore-London
  24. ↑ Peter J. Lu and Paul J. Steinhardt (2007). "Decagonal and Quasi-crystalline Tilings in Medieval Islamic Architecture" (PDF). Science 315 (5815): 1106–1110. Bibcode:2007Sci...315.1106L. doi:10.1126/science.1135491. PMID 17322056.
  25. ↑ Lu, P. J.; Steinhardt, P. J. (2007). "Decagonal and Quasi-Crystalline Tilings in Medieval Islamic Architecture". Science 315 (5815): 1106–1110. Bibcode:2007Sci...315.1106L. doi:10.1126/science.1135491. PMID 17322056.
  26. ↑ Makovicky, Emil (2007). "Comment on "Decagonal and Quasi-Crystalline Tilings in Medieval Islamic Architecture"". Science 318 (5855): 1383–1383. Bibcode:2007Sci...318.1383M. doi:10.1126/science.1146262.
  27. ↑ "Nobel win for crystal discovery". BBC News. 2011-10-05. Retrieved 2011-10-05.
  28. ↑ Bohr, H. (1925). "Zur Theorie fastperiodischer Funktionen I". Acta Mathematicae 45: 580. doi:10.1007/BF02395468.
  29. ↑ de Bruijn, N. (1981). "Algebraic theory of Penrose's non-periodic tilings of the plane". Nederl. Akad. Wetensch. Proc A84: 39.
  30. ↑ Suck, Jens-Boie; Schreiber, M.; Häussler, Peter (2002). Quasicrystals: An Introduction to Structure, Physical Properties and Applications. Springer Science & Business Media. pp. 1–. ISBN 978-3-540-64224-4.
  31. ↑ Paterson, Alan L. T. (1999). Groupoids, inverse semigroups, and their operator algebras. Springer. p. 164. ISBN 0-8176-4051-7.
  32. 1 2 Yamamoto, Akiji (2008). "Software package for structure analysis of quasicrystals". Science and Technology of Advanced Materials (free-download review) 9: 013001. Bibcode:2008STAdM...9a3001Y. doi:10.1088/1468-6996/9/3/013001.
  33. ↑ Korepin, V.E. Completely integrable models in quasicrystals. Comm. Math. Phys. Volume 110, Number 1 (1987), 157–171.
  34. ↑ MacIá, Enrique (2006). "The role of aperiodic order in science and technology". Reports on Progress in Physics 69 (2): 397–441. Bibcode:2006RPPh...69..397M. doi:10.1088/0034-4885/69/2/R03.
  35. ↑ Tsai, An Pang (2008). "Icosahedral clusters, icosaheral order and stability of quasicrystals—a view of metallurgy". Science and Technology of Advanced Materials (free-download review) 9: 013008. Bibcode:2008STAdM...9a3008T. doi:10.1088/1468-6996/9/1/013008.
  36. ↑ Louzguine-Luzgin, D. V.; Inoue, A. (2008). "Formation and Properties of Quasicrystals". Annual Review of Materials Research 38: 403–423. doi:10.1146/annurev.matsci.38.060407.130318.
  37. 1 2 3 Sputtering technique forms versatile quasicrystalline coatings, MRS BULLETIN, VOLUME 36, AUGUST 2011, www.mrs.org/bulletin, p581
  38. 1 2 Samavat, Feridoun; Tavakoli, Mohammad Hossein; Habibi, Safdar; Jaleh, Babak; Ahmad, Parisa Taravati (2012). "Quasicrystals". Open Journal of Physical Chemistry 02 (01): 7–14. doi:10.4236/ojpc.2012.21002. ISSN 2162-1969.
  39. ↑ Al-Cu-Fe QUASICRYSTALLINE COATINGS AND COMPOSITES STUDIED BY MECHANICAL SPECTROSCOPY, Jan FIKAR, THÈSE NO 2707 (2002), ÉCOLE POLYTECHNIQUE FÉDÉRALE DE LAUSANNE
  40. ↑ "Sitram - Cybernox Frypan - Cookware (description and specification)". Aviva. Retrieved 12 February 2016.
  41. 1 2 3 Matthew Kalman (12 October 2011). "The Quasicrystal Laureate". MIT Technology Review. Retrieved 12 February 2016.

Further reading

External links

This article is issued from Wikipedia - version of the Sunday, February 14, 2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.