Patterned media

Patterned media (also known as bit-patterned media or BPM[1]) is a potential future hard disk drive technology to record data in magnetic islands (one bit per island), as opposed to current hard disk drive technology where each bit is stored in 20-30 magnetic grains within a continuous magnetic film. The islands would be patterned from a precursor magnetic film using nanolithography. It is one of the proposed technologies to succeed perpendicular recording due to the greater storage densities it would enable.

Comparison with existing HDD technology

In existing hard disk drives, data is stored in a thin magnetic film. This film is deposited so that it consists of isolated (weakly exchange coupled) grains of material of around 8 nm diameter.[2] One bit of data consists of around 20-30 grains that are magnetized in the same direction (either "up" or "down", with respect to the plane of the disc). One method of increasing storage density has been to reduce the average grain volume. However, the energy barrier for thermal switching is proportional to the grain volume. With existing materials, further reductions in the grain volume would result in data loss occurring spontaneously due to superparamagnetism.

In patterned media, the thin magnetic film is first deposited so there is strong exchange coupling between the grains. Using nanolithography, it is then patterned into magnetic islands. The strong exchange coupling means that the energy barrier is now proportional to the island volume, rather than the volume of individual grains within the island. Therefore storage density increases can be achieved by patterning islands of increasingly small diameter, whilst maintaining thermal stability.[3] Patterned media is predicted to enable areal densities up to 20-300 Tb/in2 as opposed to the 1 Tb/in2 limit that exists with current HDD technology.[4]

Differences in terms of control strategies

In existing HDDs data bits are ideally written on concentric circular tracks. This process is different in bit patterned media recording where data should be written on tracks with predetermined shapes, which are created by lithography (c.f. the next section) on the disk. The trajectories that are required to be followed by the servo system in patterned media recording are characterized by a set of "servo tracks" existing on the disk. Deviation of a servo track from an ideal circular shape is called "repeatable runout" (RRO). Therefore, the servo controller in bit patterned media recording has to follow the RRO which is unknown in the time of design, and as a result the servo control methodologies used for conventional drives cannot be applied. Patterned media recording has some specific challenges in terms of servo control design which are briefly listed here:[5]

Methods of patterned media fabrication

Ion beam lithography

In preliminary research, one of the processes investigated for creating prototypes was ion beam proximity lithography. Ion beam proximity lithography uses stencil masks to produce patterns in ion-sensitive material (resist) which is transferred to magnetic material.[6] The stencil mask contains a thin free standing silicon nitride membrane in which openings are formed. The pattern to be generated is first formed on a substrate that contains a photo-resist using electron beam lithography. Next the substrate is used to transfer the given pattern onto the nitride membrane (stencil mask) using the process of plasma etching. To create sufficient substrates is to maintain size uniformity of the openings which is transferred to the mask during the fabrication process (etching). Many factors contribute to the achievement and maintenance of size uniformity in the mask, such as: pressure, temperature, energy (amount of voltage), and power used when etching. To optimize the process of etching uniform patterns correctly under these parameters, the substrate can be used as a template to fabricate stencil masks of silicone nitride through the process of ion proximity beam lithography. The stencil mask can then be used as a prototype to create pattern media.

Directed self-assembly of block copolymer films

In 2014, Ricardo Ruiz of Hitachi Global Storage Technologies writes in an upcoming-conference briefing note that "the most promising solution to the lithographic challenge can be found in directed self assembly of block copolymer films which has recently evolved as a viable technique to achieve sub-20nm lithography in time for BPM technology".[7]

See also

References

  1. ↑ "Bit-Patterned Media for High-Density HDDs". Date withheld by publisher. Retrieved 17 September 2014. Bit-patterned media (BPM) are a type of magnetic recording medium in which the magnetic layer is reduced to the size of one bit (one magnetic dot and space). Check date values in: |date= (help)
  2. ↑ Weller et al., L10 FePtX–Y media for heat-assisted magnetic recording, (2013), 210, 7, 1245-1260, Physica Status Solidi A
  3. ↑ Ross, C.A.: "Patterned magnetic recording media"p 203-235. Annual Review of Materials Science, 2001: 31.
  4. ↑ Griffiths, Rhys (25 November 2013). "Directed self-assembly of block copolymers for use in bit patterned media fabrication". Journal of Physics D: Applied Physics 46 (50). doi:10.1088/0022-3727/46/50/503001.
  5. ↑ Shahsavari; et al. (2014). "Repeatable Runout Following in Bit Patterned Media Recording". ASME 2014 Conference on Information Storage and Processing Systems: V001T03A001––V001T03A001.
  6. ↑ Wolfe et al.: A proximity ion beam lithography process for high density nanostructures.,(1996):.14, 3896-3899. Journal of Vacuum Science and Technology B
  7. ↑ "Magnetic Bit Patterned Media Fabrication Using Block Copolymer Directed Assembly". 2014. Retrieved 17 September 2014. The most promising solution to the lithographic challenge can be found in directed self assembly of block copolymer films which has recently evolved as a viable technique to achieve sub-20nm lithography in time for BPM technology.
This article is issued from Wikipedia - version of the Wednesday, September 02, 2015. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.