Grazing-incidence small-angle scattering

Grazing-incidence small-angle scattering (GISAS) is a scattering technique used to study nanostructured surfaces and thin films. The scattered probe is either photons (Grazing-incidence small-angle X-ray scattering, GISAXS) or neutrons (Grazing-incidence small-angle neutron scattering, GISANS). GISAS combines the accessible length scales of Small-angle scattering (SAS: SAXS or SANS) and the surface sensitivity of grazing incidence diffraction (GID).

Geometry of a GISAS experiment. The incident beam strikes the sample under a small angle close to the critical angle of total external x-ray reflection. The intense reflected beam as well as the intense scattering in the incident plane are attenuated by a rod-shaped beam stop. The diffuse scattering from the sample (red arrow) is recorded with an area detector. As an example the scattering from a block copolymer film with perpendicular lamellae is shown in the detector plane. The two lobes of scattering correspond to the lateral lamellar period of about 80 nm.

GISAS applications

A typical application of GISAS is the characterisation of self-assembly and self-organization on the nanoscale in thin films. Systems studied by GISAS include quantum dot arrays,[1] growth instabilities formed during in-situ growth,[2] self-organized nanostructures in thin films of block copolymers,[3] silica mesophases,[4][5] and nanoparticles.[6][7]

GISAXS was introduced by Levine and Cohen[8] to study the dewetting of gold deposited on a glass surface. The technique was further developed by Naudon[9] and coworkers to study metal agglomerates on surfaces and in buried interfaces.[10] With the advent of nanoscience other applications evolved quickly, first in hard matter such as the characterization of quantum dots on semiconductor surfaces and the in-situ characterization of metal deposits on oxide surfaces. This was soon to be followed by soft matter systems such as ultrathin polymer films,[11] polymer blends, block copolymer films and other self-organized nanostructured thin films that have become indispensable for nanoscience and technology. Future challenges of GISAS may lie in biological applications, such as proteins, peptides, or viruses attached to surfaces or in lipid layers.

GISAXS interpretation

As a hybrid technique, GISAXS combines concepts from transmission SAXS and from GID. From SAXS it uses the form factors and structure factors. From GID it uses the scattering geometry close to the critical angles of substrate and film, and the two-dimensional character of the scattering, giving rise to diffuse rods of scattering intensity perpendicular to the surface. GISAXS also shares elements of the scattering technique of diffuse reflectivity such as the Yoneda/Vinyard peak at the critical angle of the sample, and the scattering theory, the distorted wave Born approximation (DWBA).[12] However, while diffuse reflectivity remains confined to the incident plane (the plane given by the incident beam and the surface normal), GISAXS explores the whole scattering from the surface in all directions, typically utilizing an area detector. Thus GISAXS gains access to a wider range of lateral and vertical structures and, in particular, is sensitive to the morphology and preferential alignment of nanoscale objects at the surface or inside the thin film.

As a particular consequence of the DWBA, the refraction of x-rays has to be always taken into account in the case of thin film studies,[13][14] due to the fact that scattering angles are small, often less than 1 deg. The refraction correction applies to the perpendicular component of the scattering vector with respect to the substrate while the parallel component is unaffected. Thus parallel scattering can often be interpreted within the kinematic theory of SAXS, while refractive corrections apply to the scattering along perpendicular cuts of the scattering image, for instance along a scattering rod.

In the interpretation of GISAXS images some complication arises in the scattering from low-Z films e.g. organic materials on silicon wafers, when the incident angle is in between the critical angles of the film and the substrate. In this case, the reflected beam from the substrate has a similar strength as the incident beam and thus the scattering from the reflected beam from the film structure can give rise to a doubling of scattering features in the perpendicular direction. This as well as interference between the scattering from the direct and the reflected beam can be fully accounted for by the DWBA scattering theory.[14]

These complications are often more than offset by the fact that the dynamic enhancement of the scattering intensity is significant. In combination with the straightforward scattering geometry, where all relevant information is contained in a single scattering image, in-situ and real-time experiments are facilitated. Specifically self-organization during MBE growth[2] and re-organization processes in block copolymer films under the influence of solvent vapor[3] have been characterized on the relevant timescales ranging from seconds to minutes. Ultimately the time resolution is limited by the x-ray flux on the samples necessary to collect an image and the read-out time of the area detector.

Experimental practice

Dedicated or partially dedicated GISAXS beamlines exist at many Synchrotron light sources (for instance APS, CHESS, ESRF, HASYLAB, NSLS, Pohang Light Source) and also Advanced Light Source at LBNL.

At neutron research facilities, GISANS is increasingly used, typically on small-angle (SANS) instruments or on reflectometers.

GISAS does not require any specific sample preparation other than thin film deposition techniques. Film thicknesses may range from a few nm to several 100 nm, and such thin films are still fully penetrated by the x-ray beam. The film surface, the film interior, as well as the substrate-film interface are all accessible. By varying the incidence angle the various contributions can be identified.

References

  1. ↑ T. H. Metzger, I. Kegel, R. Paniago, A. Lorke, J. Peisl, J. Schulze, I. Eisele, P. Schittenhelm, and G. Abstreiter: "Shape, size, strain and correlations in quantum dot systems studied by grazing incidence X-ray scattering methods", Thin Solid Films 336,1-8 (1998).
  2. 1 2 Gilles Renaud, Rémi Lazzari, Christine Revenant, Antoine Barbier, Marion Noblet, Olivier Ulrich, Frédéric Leroy, Jacques Jupille, Yves Borensztein, Claude R. Henry, Jean-Paul Deville, Fabrice Scheurer, Jeannot Mane-Mane, and Olivier Fruchart: "Real-Time Monitoring of Growing Nanoparticles", Science 300, 1416 (2003).
  3. 1 2 Detlef-M. Smilgies, Peter Busch, Dorthe Posselt, and Christine M. Papadakis: "Characterization of Polymer Thin Films with Small-Angle X-ray Scattering under Grazing Incidence (GISAXS)", Synchrotron Radiation News, Issue 15(5), p. 35-42, 2002.
  4. ↑ A. Gibaud, D. Grosso, B. Smarsly, A. Baptiste, J. F. Bardeau, F. Babonneau, D. A. Doshi, Z. Chen, C. Jeffrey Brinker, and C. Sanchez: "Evaporation-Controlled Self-Assembly of Silica Surfactant Mesophases", J. Phys. Chem. B 107, 6114-6118 (2003).
  5. ↑ P. Chatterjee, S. Hazra and H. Amenitsch: "Substrate and drying effect in shape and ordering of micelles inside CTAB-silica mesostructured films", Soft Matter 8, 2956 (2012).
  6. ↑ S. Hazra, A. Gibaud and C. Sella: "Tunable absorption of Au-Al2O3 nanocermet thin films and its morphology", Appl. Phys. Lett. 85, 395 (2004).
  7. ↑ Aaron E. Saunders, Ali Ghezelbash, Detlef-M. Smilgies, Michael B. Sigman Jr., and Brian A. Korgel: "Columnar Self-Assembly of Colloidal Nanodisks", Nano Letters 6, 2959-2963(2006).
  8. ↑ J. R. Levine, J. B. Cohen, Y. W. Chung and P. Georgopoulos:" Grazing-incidence small-angle X-ray scattering: new tool for studying thin film growth" , J. Appl. Cryst. 22, 528-532 (1989).
  9. ↑ A. Naudon in H. Brumberger (ed.): "Modern Aspects of Small-Angle Scattering", (Kluwer Academic Publishers, Amsterdam, 1995), p. 191.
  10. ↑ S. Hazra, A. Gibaud, A. Desert, C. Sella, and A. Naudon: "Morphology of nanocermet thin films: x-ray scattering study", Physica B 283, 97 (2000).
  11. ↑ J. S. Gutmann, P. Müller-Buschbaum, D. W. Schubert, N. Stribeck, D. Smilgies, and M. Stamm: "Roughness Correlations in Ultrathin Polymer Blend Films" (Proceedings of SXNS–6), Physica B 283, 40 (2000).
  12. ↑ S. K. Sinha, E. B. Sirota, S. Garoff, and H. B. Stanley: "X-ray and neutron scattering from rough surfaces", Phys. Rev. B 38, 2297-2311 (1988); M. Rauscher, T. Salditt, and H. Spohn: "Small-angle X-ray scattering under grazing incidence: the cross section in the distorted-wave Born approximation", Phys. Rev. B, 52(23), 16855-16863, (1995); R. Lazzari: "IsGISAXS: a program for grazing-incidence small-angle X-ray scattering analysis of supported islands", J. Appl. Cryst. 35, 406-421 (2002).
  13. ↑ Byeongdu Lee, Insun Park, Jinhwan Yoon, Soojin Park, Jehan Kim, Kwang-Woo Kim, Taihyun Chang, and Moonhor Ree: "Structural Analysis of Block Copolymer Thin Films with Grazing Incidence Small-Angle X-ray Scattering", Macromolecules 38, 4311-4323(2005).
  14. 1 2 P. Busch, M. Rauscher, D.-M. Smilgies, D. Posselt, and C. M. Papadakis: "Grazing-incidence small-angle x-ray scattering (GISAXS) as a tool for the investigation of thin nanostructured block copolymer films - The scattering cross-section in the distorted wave Born approximation", J. Appl. Cryst. 39, 433-442 (2006).

External links

Portals

Tutorials

Software

This article is issued from Wikipedia - version of the Wednesday, December 16, 2015. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.