Ceramic-impregnated fabrics

Ceramic-impregnated fabrics is a fabric that has been impregnated with ceramic. Nanometric bioceramic can be incorporated into the polymer from which the fabric is manufactured. Bioceramic nanoparticles are added to the fused polymer.Some types of ceramics show thermally-induced photoluminescence, emitting light in the far infrared (FIR) region of the electromagnetic spectrum.When in contact with the body heat, the thermoluminescence of the fabrics with embedded bioceramic is enhanced. Bioceramics presents high reflection coefficient for the infrared radiation.

Method of production

One way in which fabrics can be impregnated with ceramic is the process of electrophoretic deposition or EPD in the industry. In this process nano ceramic particles are put into a solution which the fabric to be infiltrated will be placed in. The solution is then heated to high temperatures and then the fabric is placed into the solution. Next a current is passed through and the nano ceramic particles coat and impregnate the fabric. The pH level as well as the amount of time and amount of current can change the effects of how well the fabric is infiltrated and how it is coated. Other processing methods can be further broken down into what particles will be added. There are two distinct groups. The first is the SiC group which contains silicon, carbon as well as additives for oxidation processes. When it comes to using this group for the purpose of ceramic-impregnation the textile must first go under a treatment. This is usually pyrolytic carbon or BN which is deposited using a chemical vapor infiltration or CVI. Next an overlayer of SiC is deposited on the textile using the same method. After this step the matrix of the textile is infiltrated by a slurry made up of SiC particles which can be put in a polymer or they can simply be just molten SiC. This process coats the entirety of the textile. The other group is the oxide group. Oxides commonly used are alumina, silica, mullite, and rare-earth phosphates. The process for impregnation is quite simple. A slurry is prepared with the oxide desired and the textile is placed in it. Again the slurry can be a molten state or a polymer based one. There are a few differences between these groups however. The SiC group has over twice the fracture strength and thermal conductivity when compared to the Oxides group. However the oxides are more stable in combustion and oxidizing environments. The process by which the textile is impregnated depends on what materials will be used, as well as the intended purpose of that fabric.

Uses

Woven ceramic fabrics allow for the opportunity to create new, imaginative solutions for previously impossible problems. These Fabrics are utilized for thermal, mechanical and electrical applications for a variety of reasons. Ceramic impregnated fabrics are most importantly used in 3 main fields, Aerospace, Electronic, and Industrial. In Aerospace the fabrics are used in Space Shuttles for the Exit cone, Door seals, Micrometeorite shield, Gaskets, Booster access doors, Shuttle tiles, and in the Whipple shield. Ceramic Impregnated Fabrics are utilized in Aerospace because they have low thermal conductivity and can be fabricated into high temperature thermal insulators. In the Electronic Industry the fabrics are used primarily for insulation and seals because of its low porosity it makes a great insulator. Ceramic Fabrics Industrial uses include Furnace linings, Furnace zone dividers, door seals, tube seals, gaskets, and expansion joints. In addition to being a great thermal insulator, these fabrics do not shrink or elongate with high temperature changes making them great for industrial uses that involve high temperatures.

References

Boccaccini, A.R. ; Kaya, C. ; Chawla, K.K. Composites Part A, 2001, Vol.32(8), pp. 997–1006 [Peer Reviewed Journal]

Binetruy, Christophe, and Fancois Boussu. "Recent Advances in Textile Composites: October 26–28, 2010, Lille Grand Palais, Lille, France." Google Books. DEStech Publications Inc, 26 Oct. 2010. Web. 07 Dec. 2013.

Integral Textile Ceramic StructuresAnnual Review of Materials Research Vol. 38: 425–443 (Volume publication date August 2008) First published online as a Review in Advance on March 26, 2008 DOI: 10.1146/annurev.matsci.38.060407.130214

"Thermal Insulation Property of Spacer Fabrics Integrated by Ceramic Powder Impregnated Fabrics." Thermal Insulation Property of Spacer Fabrics Integrated by Ceramic Powder Impregnated Fabrics. N.p., n.d. Web. 08 Dec. 2013.

Sawko, Paul M., and Huy Kim Tran. Strength and flexibility properties of advanced ceramic fabrics. Moffett Field, Calif.: National Aeronautics and Space Administration, Ames Research Center ;, 1985. Print.