Direct reduced iron

Direct-reduced iron (DRI), also called sponge iron,[1] is produced from direct reduction of iron ore (in the form of lumps, pellets or fines) by a reducing gas produced from natural gas or coal. The reducing gas is a mixture, the majority of which is hydrogen (H2) and carbon monoxide (CO) which act as reducing agents. This process of reducing the iron ore in solid form by reducing gases is called direct reduction.

Need for this

The conventional route for making steel consists of sintering or pelletization plants, coke ovens, blast furnaces, and basic oxygen furnaces. Such plants require high capital expenses and raw materials of stringent specifications. Coking coal is needed to make a coke strong enough to support the burden in the blast furnace. Integrated steel plants of less than one million tons annual capacity are generally not economically viable. The coke ovens and sintering plants in an integrated steel plant are polluting and expensive units. Slag is less dense than iron.

Process

Direct reduction, an alternative route of iron making, has been developed to overcome some of these difficulties of conventional blast furnaces. DRI is successfully manufactured in various parts of the world through either natural gas or coal-based technology. Iron ore is reduced in solid state at 800 to 1,050 °C (1,470 to 1,920 °F) either by reducing gas (H2+CO) or coal. The specific investment and operating costs of direct reduction plants are low compared to integrated steel plants and are more suitable for many developing countries where supplies of coking coal are limited.

The direct reduction process is energy efficient, but is most competitive with the blast furnace when it can be integrated with electric arc furnaces to take advantage of the latent heat produced by the DRI product.[2]

Factors that help make DRI economical:

India is the world’s largest producer of direct-reduced iron, a vital constituent of the steel industry. Many other countries use variants of the process, so providing iron for local engineering industries.

Problems

Directly reduced iron is highly susceptible to oxidation and rusting if left unprotected, and is normally quickly processed further to steel. The bulk iron can also catch fire since it is pyrophoric.[3]

History

Main article: Bloomery

Producing sponge iron and then working it was the earliest method used to obtain iron in the Middle East, Egypt, and Europe, where it remained in use until at least the 16th century. There is some evidence that the bloomery method was also used in China, but China had developed blast furnaces to obtain pig iron by 500 BCE.

The advantage of the bloomery technique is that iron can be obtained at a lower furnace temperature, only about 1,100°C or so. The disadvantage, relatively to using a blast furnace, is that only small quantities can be made at a time.

Uses

Sponge iron is not useful by itself, but can be processed to create wrought iron. The sponge is removed from the furnace, called a bloomery, and repeatedly beaten with heavy hammers and folded over to remove the slag, oxidise any carbon or carbide and weld the iron together. This treatment usually creates wrought iron with about three percent slag and a fraction of a percent of other impurities. Further treatment may add controlled amounts of carbon, allowing various kinds of heat treatment (e.g. "steeling").

Today, sponge iron is created by reducing iron ore without melting it. This makes for an energy-efficient feedstock for specialty steel manufacturers which used to rely upon scrap metal.

See also

Article On DRI

References

Notes
  1. ↑ "What is direct reduced iron (DRI)? definition and meaning". Businessdictionary.com. Retrieved 2011-07-11.
  2. ↑ R. J. Fruehan, et al. (2000). Theoretical Minimum Energies to Produce Steel (for Selected Conditions)
  3. ↑ Hattwig, Martin; Steen, Henrikus (2004), Handbook of explosion prevention and protection, Wiley-VCH, pp. 269–270, ISBN 978-3-527-30718-0.
Bibliography

External links