Buckypaper

Buckypaper made of carbon nanotubes

Buckypaper is a thin sheet made from an aggregate of carbon nanotubes[1] or carbon nanotube grid paper. The nanotubes are approximately 50,000 times thinner than a human hair. Originally, it was fabricated as a way to handle carbon nanotubes, but it is also being studied and developed into applications by several research groups, showing promise as vehicle armor, personal armor, and next-generation electronics and displays.

Background

Buckypaper is a macroscopic aggregate of carbon nanotubes (CNT), or "buckytubes". It owes its name to the buckminsterfullerene, the 60 carbon fullerene (an allotrope of carbon with similar bonding that is sometimes referred to as a "Buckyball" in honor of R. Buckminster Fuller).[1]

Synthesis

The generally accepted methods of making CNT films involves the use of non-ionic surfactants, such as Triton X-100[2] and sodium lauryl sulfate,[3] which improves their dispersibility in aqueous solution. These suspensions can then be membrane filtered under positive or negative pressure to yield uniform films.[4] The van der Waals force's interaction between the nanotube surface and the surfactant can often be mechanically strong and quite stable and therefore there are no assurances that all the surfactant is removed from the CNT film after formation. Washing with methanol, an effective solvent in the removal of Triton X, was found to cause cracking and deformation of the film. It has also been found that Triton X can lead to cell lysis and in turn tissue inflammatory responses even at low concentrations.[5]

In order to avoid adverse side-effects from the possible presence of surfactants, an alternative casting process can be used involving a frit compression method that did not require the use of surfactants or surface modification.[6] The dimensions can be controlled through the size of the syringe housing and through the mass of carbon nanotubes added. Their thicknesses are typically much larger than surfactant-cast buckypaper and have been synthesized from 120 μm up to 650 μm; whilst no nomenclature system exists to govern thicknesses for samples to be classified as paper, samples with thicknesses greater than 500 μm are referred to as buckydiscs. The frit compression method allows rapid casting of buckypaper and buckydiscs with recovery of the casting solvent and control over the 2D and 3D geometry.

Aligned multi-walled carbon nanotube (MWNT) growth has been used in CNT film synthesis through the domino effect.[7] In this process, "forests" of MWNTs are pushed flat in a single direction, compressing their vertical orientation into the horizontal plane, which results in the formation of high-purity buckypaper with no further purification or treatment required. By comparison, when a buckypaper sample was formed from the 1 ton compression of chemical vapor deposition (CVD) generated MWNT powder, any application of a solvent led to the immediate swelling of the film till it reverted into particulate matter. It appears that for the CNT powder used, compression alone was insufficient to generate robust buckypaper and highlights that the aligned growth methodology generates in-situ tube-tube interactions not found in CVD CNT powder and are preserved through to the domino pushing formation of buckypaper.

Properties

Buckypaper is one tenth the weight yet potentially 500 times stronger than steel when its sheets are stacked to form a composite.[1] It could disperse heat like brass or steel and it could conduct electricity like copper or silicon.[1] Rice University scientist Wade Adams says, "All those things are what a lot of people in nanotechnology have been working toward as sort of Holy Grails."[8]

Applications

Among the possible uses for buckypaper that are being researched:

See also

References

  1. 1.0 1.1 1.2 1.3 "Future planes, cars may be made of `buckypaper'". Yahoo! Tech News. 2008-10-17. Retrieved 2008-10-18.
  2. Panhuis MIH, Salvador-Morales C, Franklin E, Chambers G, Fonseca A and Nagy JB, et al. "Characterization of an interaction between functionalized carbon nanotubes and an enzyme". J Nanosci Nanotechnology 3 (2003) 209
  3. Sun J and Gao L. "Development of a dispersion process for carbon nanotubes in ceramic matrix by heterocoagulation". Carbon 41 (2003) 1063
  4. Vohrer U, Kolaric I, Haque MH, Roth S and Detlaff-Weglikowska U. "Carbon nanotube sheets for the use as artificial muscles" Carbon 42 (2004) 1159
  5. Cornett JB and Shockman GD. "Cellular lysis of Streptococcus faecalis induced with Triton X-100" J Bacteriol 135 (1978) 153
  6. Whitby RLD, Fukuda T, Maekawa T, James SL, Mikhalovsky SV, "Geometric control and tuneable pore size distribution of buckypaper and buckydiscs" Carbon 46 (2008) 949
  7. Wang D, Song PC, Liu CH, Wu W, Fan SS, "Highly oriented carbon nanotube papers made of aligned carbon nanotubes" Nanotechnology 19 (2008) 075609
  8. "Nanotechnology to soon provide paper stronger than steel for commercial uses" James B. Lewis, the Foresight Institute 2008-10-24. Retrieved 2012-12-7.
  9. Z. Zhao and J. Gou "Improved fire retardancy of thermoset composites modified with carbon nanofibers" Sci. Technol. Adv. Mater. 10 (2009) 015005 free download

External links