Borazon is a brand name of a cubic form of boron nitride (cBN). Its color ranges from black to brown and gold, depending on the chemical bond. It is one of the hardest known materials, along with various forms of diamond and boron nitride. Borazon is a crystal created by heating equal quantities of boron and nitrogen at temperatures greater than 1800 °C (3300 °F) at 7 GPa (1 million lbf/in2).

Borazon was first produced in 1957 by Robert H. Wentorf, Jr., a physical chemist working for the General Electric Company.[1] In 1969, General Electric adopted the name Borazon as its trademark for the material.

Uses and production

Borazon is used for a number of things, such as: cutting tools, dies, punches, shears, knives, saw blades, bearing rings, needles, rollers, spacers, balls, pump, compressor parts, engine & drive train components (e.g. camshafts, crankshafts, gears, valve stems, drive shafts, CV joints, piston pins, fuel injectors, turbochargers, and aerospace and land-based gas turbine parts such as vanes, blades, nozzles, and seals), surgical knives, blades, scissors, honing, superfinishing, cylinder liners, connecting rods, grinding of steel and paper mill rolls, and gears.

Prior to the production of Borazon, diamond was the preferred abrasive used for grinding very hard superalloys but it could not be used effectively on steels because carbon tends to dissolve in iron at high temperatures. Aluminium oxide was the conventional abrasive used on hardened steel tools.[2]

Borazon replaced aluminium oxide for grinding hardened steels due to its far superior abrasive properties, comparable to that of diamond.[2] Borazon is used in industrial applications to shape tools, as it can withstand temperatures greater than 2000 °C (3632 °F), much higher than that of a pure diamond at 871 °C (1600 °F).[3] Other uses include jewellery designing, glass cutting and laceration of diamonds.

CBN-coated grinding wheels, referred to as Borazon wheels, are routinely used in the machining of hard ferrous metals, cast irons, and nickel-base and cobalt-base superalloys. They can grind more material, to a higher degree of accuracy, than any other abrasive. The limiting factor in the life of such tools is typically determined not by wear on the cutting surface but by its break-down and separation from the metal core resulting from failure of the bonding layer.[2]

See also

References

  1. ↑ R. H. Wentorf (1957). "Cubic Form of Boron Nitride". J. Chem. Phys. 26 (4): 956. doi:10.1063/1.1745964.
  2. ↑ 2.0 2.1 2.2 Description of Borazon and Borozon as prior art in patent from 31 December 1969
  3. ↑ "13.5 Properties of diamond and cubic boron nitride". Landolt-Börnstein - Group VIII Advanced Materials and Technologies: Powder Metallurgy Data. Refractory, Hard and Intermetallic Materials 2A2. pp. 118–139. doi:10.1007/b83029. ISBN 978-3-540-42961-6.

External links