ASTM F568M

ASTM F568M is an ASTM International standard for metric bolts, screws and studs that are used in general engineering applications. It is titled: Standard Specification for Carbon and Alloy Steel Externally Threaded Metric Fasteners. It defines mechanical properties for fasteners that range from M1.6 to 100 in diameter. The standard was withdrawn in 2012.^[1]

This standard defines property classes, the metric equivalent of a screw grade, that are almost identical to those defined by ISO 898-1, except for the addition of the 8.8.3 and 10.9.3 standards. These two additional standards are fasteners that have the same mechanical properties as their base property class (i.e. 8.8 and 10.9), but are made from weathering steel.^[1][2]

This is a standard set by the standards organization ASTM International, a voluntary standards development organizations that sets technical standards for materials, products, systems, and services.

Mechanical properties

Head markings and mechanical properties^[3]

Head marking	Grade, material & condition	Nominal size range [mm]	Proof strength [MPa]	Yield strength (min) [MPa]	Tensile strength (min) [MPa]	Core hardness [Rockwell]
	Class 4.6 Low or medium carbon steel	5–100	225	240	400	B67–95
	Class 4.8 Low or medium carbon steel; fully or partially annealed	1.6–16	310	340	420	B71–95
	Class 5.8 Low or medium carbon steel; cold worked	5–24	380	420	520	B82–95
	Class 8.8[4] Medium carbon steel; quench and tempered	Under 16 (inc.)	580	640	800
		17–72	600	660	830	C23–34
	Class 8.8 low carbon Low carbon boron steel; quench and tempered
	Class 8.8.3[1] Atmospheric corrosion resistant steel; quench and tempered
	Class 9.8 Medium carbon steel; quench and tempered	1.6–16	650	720	900	C27–36
	Class 9.8 low carbon Low carbon boron steel; quench and tempered
	Class 10.9 Alloy steel; quench and tempered	5–100	830	940	1040	C33–39
	Class 10.9 low carbon Low carbon boron steel; quench and tempered
	Class 10.9.3[1] Atmospheric corrosion resistant steel; quench and tempered
	Class 12.9 Alloy steel; quench and tempered	1.6–100	970	1100	1220	C38–44