Polyester

SEM picture of a bend in a high-surface area polyester fiber with a seven-lobed cross section

Close-up of a polyester shirt

Polyester is a category of polymers which contain the ester functional group in their main chain. Although there are many polyesters, the term "polyester" as a specific material most commonly refers to polyethylene terephthalate (PET). Polyesters include naturally occurring chemicals, such as in the cutin of plant cuticles, as well as synthetics through step-growth polymerization such as polycarbonate and polybutyrate. Natural polyesters and a few synthetic ones are biodegradable, but most synthetic polyesters are not.

Depending on the chemical structure, polyester can be a thermoplastic or thermoset, there are also polyester resins cured by hardeners; however, the most common polyesters are thermoplastics.^[1]

Fabrics woven or knitted from polyester thread or yarn are used extensively in apparel and home furnishings, from shirts and pants to jackets and hats, bed sheets, blankets, upholstered furniture and computer mouse mats. Industrial polyester fibers, yarns and ropes are used in tyre reinforcements, fabrics for conveyor belts, safety belts, coated fabrics and plastic reinforcements with high-energy absorption. Polyester fiber is used as cushioning and insulating material in pillows, comforters and upholstery padding. Polyesters are also used to make bottles, films, tarpaulin, canoes, liquid crystal displays, holograms, filters, dielectric film for capacitors, film insulation for wire and insulating tapes. Polyesters are widely used as a finish on high-quality wood products such as guitars, pianos and vehicle/yacht interiors. Thixotropic properties of spray-applicable polyesters make them ideal for use on open-grain timbers, as they can quickly fill wood grain, with a high-build film thickness per coat. Cured polyesters can be sanded and polished to a high-gloss, durable finish.

While synthetic clothing in general is perceived by many as having a less natural feel compared to fabrics woven from natural fibers (such as cotton and wool)^{[citation needed]}, polyester fabrics can provide specific advantages over natural fabrics, such as improved wrinkle resistance, durability and high color retention. As a result, polyester fibers are sometimes spun together with natural fibers to produce a cloth with blended properties. Synthetic fibers also can create materials with superior water, wind and environmental resistance compared to plant-derived fibers, and are sometimes renamed so as to suggest their similarity or even superiority to natural fibers (for example, China silk, which is a term in the textiles industry for a 100% polyester fiber woven to resemble the sheet and durability of insect-derived silk).

Liquid crystalline polyesters are among the first industrially used liquid crystal polymers. They are used for their mechanical properties and heat-resistance. These traits are also important in their application as an abradable seal in jet engines^{[citation needed]}.

Types

Polyesters as thermoplastics may change shape after the application of heat. While combustible at high temperatures, polyesters tend to shrink away from flames and self-extinguish upon ignition. Polyester fibers have high tenacity and E-modulus as well as low water absorption and minimal shrinkage in comparison with other industrial fibers.

Unsaturated polyesters (UPR) are thermosetting resins. They are used as casting materials, fiberglass laminating resins and non-metallic auto-body fillers. Fiberglass-reinforced unsaturated polyesters find wide application in bodies of yachts and as body parts of cars.

According to the composition of their main chain, polyesters can be:

Increasing the aromatic parts of polyesters increases their glass transition temperature, melting temperature, thermal stability, chemical stability...

Polyesters can also be telechelic oligomers like the polycaprolactone diol (PCL) and the polyethylene adipate diol (PEA). They are then used as prepolymers.

Industry

Basics

Polyester is a synthetic polymer made of purified terephthalic acid (PTA) or its dimethyl ester dimethyl terephthalate (DMT) and monoethylene glycol (MEG). With 18% market share of all plastic materials produced, it ranges third after polyethylene (33.5%)^{[citation needed]} and polypropylene (19.5%).

The main raw materials are described as follows:

• Purified terephthalic acid – PTA – CAS-No.: 100-21-0

Synonym: 1,4 benzenedicarboxylic acid,

Sum formula; C₆H₄(COOH)₂ , mol weight: 166.13

• Dimethylterephthalate – DMT – CAS-No: 120-61-6

Synonym: 1,4 benzenedicarboxylic acid dimethyl ester

Sum formula C₆H₄(COOCH₃)₂ , mol weight: 194.19

• Mono Ethylene Glycol – MEG – CAS No.: 107-21-1

Synonym: 1,2 ethanediol

Sum formula: C₂H₆O₂ , mol weight: 62,07

To make a polymer of high molecular weight a catalyst is needed. The most common catalyst is antimony trioxide (or antimony tri acetate):

Antimony trioxide – ATO – CAS-No.: 1309-64-4 Molecular weight: 291.51 Sum formula: Sb₂O₃

In 2008, about 10,000 tonnes Sb₂O₃ were used to produce around 49 million tonnes polyethylene terephthalate.^{[citation needed]}

Polyester is described as follows:

Polyethylene Terephthalate CAS-No.: 25038-59-9 Synonym/abbreviations: polyester, PET, PES Sum Formula: H-[C₁₀H₈O₄]-n=60–120 OH, molelcular unit weight: 192.17

There are several reasons for the importance of Polyester:

• The relatively easy accessible raw materials PTA or DMT and MEG
• The very well understood and described simple chemical process of polyester synthesis
• The low toxicity level of all raw materials and side products during polyester production and processing
• The possibility to produce PET in a closed loop at low emissions to the environment
• The outstanding mechanical and chemical properties of polyester
• The recyclability
• The wide variety of intermediate and final products made of polyester.

In table 1 the estimated world polyester production is shown. Main applications are textile polyester, bottle polyester resin, film polyester mainly for packaging and specialty polyesters for engineering plastics. According to this table, the world's total polyester production might exceed 50 million tons per annum before the year 2010.

Table 1: World polyester production

Raw material producer

Polyester processing

After the first stage of polymer production in the melt phase, the product stream divides into two different application areas which are mainly textile applications and packaging applications. In table 2, the main applications of textile and packaging of polyester is listed.

Table 2: Textile and packaging polyester application list

Abbreviations: PSF = Polyester Staple Fiber; POY = Partially Oriented Yarn; DTY = Draw Textured Yarn; FDY = Fully Drawn Yarn; CSD = Carbonated Soft Drink; A-PET = Amorphous Polyester Film; BO-PET = Biaxial Oriented Polyester Film;

A comparable small market segment (much less than 1 million tonnes/year) of polyester is used to produce engineering plastics and masterbatch.

In order to produce the polyester melt with a high efficiency, high-output processing steps like staple fiber (50–300 tonnes/day per spinning line) or POY /FDY (up to 600 tonnes/day split into about 10 spinning machines) are meanwhile more and more vertically integrated direct processes. This means the polymer melt is directly converted into the textile fibers or filaments without the common step of pelletizing. We are talking about full vertical integration when polyester is produced at one site starting from crude oil or distillation products in the chain oil → benzene → PX → PTA → PET melt → fiber/filament or bottle-grade resin. Such integrated processes are meanwhile established in more or less interrupted processes at one production site. Eastman Chemicals were the first to introduce the idea of closing the chain from PX to PET resin with their so-called INTEGREX process. The capacity of such vertically integrated production sites is >1000 tonnes/day and can easily reach 2500 tonnes/day.

Besides the above mentioned large processing units to produce staple fiber or yarns, there are ten thousands of small and very small processing plants, so that one can estimate that polyester is processed and recycled in more than 10 000 plants around the globe. This is without counting all the companies involved in the supply industry, beginning with engineering and processing machines and ending with special additives, stabilizers and colors. This is a gigantic industry complex and it is still growing by 4–8% per year, depending on the world region.

Synthesis

Synthesis of polyesters is generally achieved by a polycondensation reaction. See "condensation reactions in polymer chemistry". The general equation for the reaction of a diol with a diacid is :

(n+1) R(OH)₂ + n R´(COOH)₂ → HO[ROOCR´COO]_nROH + 2n H₂O

Azeotrope esterification

In this classical method, an alcohol and a carboxylic acid react to form a carboxylic ester. To assemble a polymer, the water formed by the reaction must be continually removed by azeotrope distillation.

Alcoholic transesterification

Transesterification: An alcohol-terminated oligomer and an ester-terminated oligomer condense to form an ester linkage, with loss of an alcohol. R and R' are the two oligomer chains, R'' is a sacrificial unit such as a methyl group (methanol is the byproduct of the esterification reaction).

Acylation (HCl method)

The acid begins as an acid chloride, and thus the polycondensation proceeds with emission of hydrochloric acid (HCl) instead of water. This method can be carried out in solution or as an enamel.

Silyl method

In this variant of the HCl method, the carboxylic acid chloride is converted with the trimethyl silyl ether of the alcohol component and production of trimethyl silyl chloride is obtained

Acetate method (esterification)

Silyl acetate method

Ring-opening polymerization

Aliphatic polyesters can be assembled from lactones under very mild conditions, catalyzed anionically, cationically or metallorganically. A number of catalytic methods for the copolymerization of epoxides with cyclic anhydrides have also recently been shown to provide a wide array of functionalized polyesters, both saturated and unsaturated.

Biodegradation

The futuro house was made of fibreglass-reinforced polyester plastic; polyester-polyurethane, and poly(methylmethacrylate) one of them was found to be degrading by Cyanobacteria and Archaea.^[2][3]

See also

• Lipase catalyzed polyesterification: Enzyme-Catalyzed Polymerization of End-Functionalized Polymers in a Microreactor

Cross-linking

Unsaturated polyesters are thermosetting resins. They are generally copolymers prepared by polymerizing one or more diol with saturated and unsaturated dicarboxylic acids (maleic acid, fumaric acid...) or their anhydrides. The double bond of unsaturated polyesters reacts with a vinyl monomer, usually styrene, resulting in a 3-D cross-linked structure. This structure acts as a thermoset. The exothermic cross-linking reaction is initiated through a catalyst, usually an organic peroxide such as methyl ethyl ketone peroxide or benzoyl peroxide.

See also

• Oligoester
• Polyester resin

References

Further reading

• Textiles, by Sara Kadolph and Anna Langford. 8th Edition, 1998.

External links

• Polyester manufacturing process
• PTA
• DMT
• MEG

v t e Fabric Woven Aertex Airdura Airguard Barathea Barkcloth Batiste Bedford cord Bengaline silk Beta cloth Bombazine Brilliantine Broadcloth Buckram Bunting Burlap C change Calico Cambric Canvas Chambray Capilene Cedar bark Challis Char cloth Charmeuse Charvet Cheesecloth Chiffon Chino Chintz Cloqué Cloth of gold Cordura Corduroy Duck Coutil Crape Cretonne Dazzle Denim Dimity Donegal tweed Dornix Dowlas Drill Drugget Flannel Foulard Fustian Gabardine Gauze Gazar Georgette Ghalamkar Gingham Grenadine Grenfell Cloth Grosgrain Habutai Haircloth Harris Tweed Herringbone Himroo Hodden Irish linen Jamdani Kerseymere Khādī Khaki drill Kente cloth Lamé Lawn Linsey-woolsey Loden Longcloth Lumalive Mackinaw Madapolam Madras Moleskin Muslin Nainsook Nankeen Ninon Oilskin Organdy Organza Osnaburg Ottoman Oxford Paduasoy Percale Pongee Poplin Rakematiz Rayadillo Rep Rinzu Ripstop Russell cord Saga Nishiki Samite Sateen Satin Saye Scarlet Seersucker Serge Scrim Shot silk Stuff Taffeta Tais Toile Tucuyo Tweed Twill Ultrasuede Ventile Vinyl coated polyester Viyella Voile Wadmal Wigan Whipcord Zephyr Zorbeez Figured woven Brocade Camlet Damask Lampas Songket Pile woven Baize Chenille Corduroy Crimplene Fustian Mockado Moquette Plush Polar fleece Terrycloth Velours du Kasaï Velvet Velveteen Zibeline Nonwoven Felt Cedar bark Knitted Boiled wool Coolmax Machine knitting Milliskin Jersey Velour Netted Bobbinet Carbon fiber Fishnet Lace Mesh Needlerun Net Ninon Tulle Technical Ballistic nylon Ban-Lon Conductive Darlexx E-textiles Gannex Gore-Tex Silnylon Spandex Stub-tex SympaTex Windstopper Patterns Argyle Bizarre silk Chiné Herringbone Houndstooth Paisley Pin stripes Shweshwe Tartan (Plaid) Tattersall Textile fibers Acrylic Alpaca Angora Cashmere Coir Cotton Hemp Jute Kevlar Linen Mohair Nylon Microfiber Olefin Pashmina Polyester Piña Ramie Rayon Sea silk Silk Sisal Spandex Spider silk Wool Finishing and printing Androsia Batik Beetling Bingata Bògòlanfini Calendering Decatising Finishing Fulling Heatsetting Mercerization Moire Nap Rogan printing Rōketsuzome Roller printing Sanforization Tenterhook Textile printing Warp printing Waxed cotton Woodblock printing Indienne Related Dyeing Fiber History of textiles History of silk Knitting Pandy Shrinkage Swatches and strike-offs Synthetic fabric Terminology Manufacturing Preservation Weaving Yarn