Phase-change material

From Wikipedia, the free encyclopedia

A sodium acetate heating pad. When the sodium acetate solution crystallises, it becomes warm.

A phase-change material (PCM) is a substance with a high heat of fusion which, melting and solidifying at a certain temperature, is capable of storing and releasing large amounts of energy. Heat is absorbed or released when the material changes from solid to liquid and vice versa; thus, PCMs are classified as latent heat storage (LHS) units.

Characteristics and classification

PCMs latent heat storage can be achieved through solid–solid, solid–liquid, solid–gas and liquid–gas phase change. However, the only phase change used for PCMs is the solid–liquid change. Liquid-gas phase changes are not practical for use as thermal storage due to the large volumes or high pressures required to store the materials when in their gas phase. Liquid–gas transitions do have a higher heat of transformation than solid–liquid transitions. Solid–solid phase changes are typically very slow and have a rather low heat of transformation.

Initially, the solid–liquid PCMs behave like sensible heat storage (SHS) materials; their temperature rises as they absorb heat. Unlike conventional SHS, however, when PCMs reach the temperature at which they change phase (their melting temperature) they absorb large amounts of heat at an almost constant temperature. The PCM continues to absorb heat without a significant rise in temperature until all the material is transformed to the liquid phase. When the ambient temperature around a liquid material falls, the PCM solidifies, releasing its stored latent heat. A large number of PCMs are available in any required temperature range from −5 up to 190 °C.^[1] Within the human comfort range between 20–30°C, some PCMs are very effective. They store 5 to 14 times more heat per unit volume than conventional storage materials such as water, masonry or rock.^[2]

Organic PCMs

Paraffin (C_nH_2n+2) and fatty acids (CH₃(CH₂)_2nCOOH)^[3]

Advantages
1. Freeze without much supercooling
2. Ability to melt congruently
3. Self nucleating properties
4. Compatibility with conventional material of construction
5. No segregation
6. Chemically stable
7. High heat of fusion
8. Safe and non-reactive
9. Recyclable
Disadvantages
1. Low thermal conductivity in their solid state. High heat transfer rates are required during the freezing cycle
2. Volumetric latent heat storage capacity is low
3. Flammable. This can be easily alleviated by a proper container
4. To obtain reliable phase change points, most manufacturers use technical grade paraffins which are essentially paraffin mixture(s) and are completely refined of oil, resulting in high costs

Inorganic

Salt hydrates (M_nH₂O)^[4]

Advantages
1. High volumetric latent heat storage capacity
2. Availability and low cost
3. Sharp melting point
4. High thermal conductivity
5. High heat of fusion
6. Non-flammable
Disadvantages
1. Change of volume is very high
2. Super cooling is major problem in solid–liquid transition
3. Nucleating agents are needed and they often become inoperative after repeated cycling

Eutectics

Organic-organic, organic-inorganic, inorganic-inorganic compounds

Advantages
1. Eutectics have sharp melting point similar to pure substance
2. Volumetric storage density is slightly above organic compounds
Disadvantages
1. Only limited data is available on thermo-physical properties as the use of these materials are very new to thermal storage application

Hygroscopic materials

Many natural building materials are hygroscopic, that is they can absorb (water condenses) and release water (water evaporates). The process is thus:

Condensation (gas to liquid) ΔH<0; enthalpy decreases (exothermic process) gives off heat.
Vaporization (liquid to gas) ΔH>0; enthalpy increases (endothermic process) absorbs heat (or cools).

Whilst this process liberates a small quantity of energy, large surfaces area allows significant (1–2 °C) heating or cooling in buildings. The corresponding materials are wool insulation, earth/clay render finishes, etc.

Selection criteria

Thermodynamic properties. The phase change material should possess:^[5]
1. Melting temperature in the desired operating temperature range
2. High latent heat of fusion per unit volume
3. High specific heat, high density and high thermal conductivity
4. Small volume changes on phase transformation and small vapor pressure at operating temperatures to reduce the containment problem
5. Congruent melting

Kinetic properties
1. High nucleation rate to avoid supercooling of the liquid phase
2. High rate of crystal growth, so that the system can meet demands of heat recovery from the storage system

Chemical properties
1. Chemical stability
2. Complete reversible freeze/melt cycle
3. No degradation after a large number of freeze/melt cycle
4. Non-corrosiveness, non-toxic, non-flammable and non-explosive materials

Economic properties
1. Low cost
2. Availability

Thermophysical properties of selected PCMs

Material	Organic PCM	Melting point ^oC	Heat of fusion kJ·kg⁻¹	Heat of fusion MJ·m⁻³	c_p solid kJ·kg⁻¹·K⁻¹	c_p liquid kJ·kg⁻¹·K⁻¹	ρ solid kg·m⁻³	ρ liquid kg·m⁻³	k solid W·m⁻¹·K⁻¹	VHC solid kJ·m⁻³·K⁻¹	VHC liquid kJ·m⁻³·K⁻¹	e solid J·m⁻²·K⁻¹·s^−1/2	Cost USD·kg⁻¹
Water	No	50000000000000000000	7002333600000000000333.6	7002319800000000000319.8	70002050099999999992.05	70004186000000000004.186	7002917000000000000917	70031000000000000001,000	70001910000000000001.6^[6]-2.22^[7]	70031880000000000001,880	70034186000000000004,186	70031890000000000001,890	69973125000000000000.003125^[8]
Sodium sulfate (Na₂SO₄·10H₂O)	No	32.4	252										0.05 ^[9]
NaCl·Na₂SO₄·10H₂O	No	18	286										0.05 ^[10]
Lauric acid	Yes^[11]^[12]	700144200000000000044.2^[13]	7002211600000000000211.6	7002197700000000000197.7	70001760000000000001.76	70002270000000000002.27	70031007000000000001,007	7002862000000000000862	?	70031772000000000001,772	70031957000000000001,957	?	70001600000000000001.6 ^[14]^[15]
TME(63%w/w)+H₂O(37%w/w)	Yes^[11]^[12]	700129800000000000029.8	7002218000000000000218.0	7002240900000000000240.9	70002750000000000002.75	70003580000000000003.58	70031120000000000001,120	70031090000000000001,090	?	70033080000000000003,080	70033902000000000003,902	?	?
Mn(NO₃)₂·6H₂O+MnCl₂·4H₂O(4%w/w)	No^[16]^[17]	700120000000000000015–25	7002125900000000000125.9	7002221800000000000221.8	70002340000000000002.34	70002779900000999992.78	70031795000000000001,795	70031728000000000001,728	?	70034200000000000004,200	70034804000000000004,804	?	?
Na₂SiO₃·5H₂O	No^[16]^[17]	700172200000000000072.20	7002267000000000000267.0	7002364500000000000364.5	70003830000000000003.83	70004570000000000004.57	70031450000000000001,450	70031280000000000001,280	69991155000000000000.103−0.128^[18]	70035554000000000005,554	70035850000000000005,850	7002801000000000000801	70008039999999999998.04^[19]
Aluminium	No	7002660320000000000660.32	7002396900000000000396.9	70031007200000000001,007.2	69998969000000000000.8969	?	70032700000000000002,700	70032375000000000002,375	7002237000000000000237^[20]^[21]	70032422000000000002,422	?	700423960000000000023,960	70002046260000000002.04626^[22]
Copper	No	70031084620000999991,084.62	7002208700000000000208.7	70031769500000000001,769.5	69993846000000000000.3846	?	70038940000000000008,940	70038020000000000008,020	7002401000000000000401^[23]	70033438000000000003,438	?	700437130000000000037,130	70006812560000000006.81256^[24]
Gold	No	70031064180000000001,064.18	700163720000000000063.72	70031166300000000001,166.3	69991290000000000000.129	?	700419300000000000019,300	700417310000000000017,310	7002318000000000000318^[25]	70032491000000000002,491	?	700428140000000000028,140	700434297800000000034,297.8^[24]
Iron	No	70031538000000000001,538	7002247300000000000247.3	70031836600000000001,836.6	69994495000000000000.4495	?	70037874000000000007,874	70036980000000000006,980	700180400000000000080.4^[26]	70033539000000000003,539	?	700416870000000000016,870	69993247900000000000.3248^[27]
Lead	No	7002327450000000000327.46	700123020000000000023.02	7002253200000000000253.2	69991286000000999990.1286	?	700411340000000000011,340	700410660000000000010,660	700135300999990000035.3^[28]	70031459000000000001,459	?	70037180000000000007,180	70002115100000000002.1151^[24]
Lithium	No	7002180540000000000180.54	7002432200000000000432.2	7002226000000000000226.0	70003581600000000003.5816	?	7002534000000000000534	7002512000000000000512	700184800000000000084.8^[29]	70031913000000000001,913	?	700412740000000000012,740	700162216400000000062.2164^[30]
Silver	No	7002961780000000000961.78	7002104600000000000104.6	70031035800000000001,035.8	69992350000000000000.235	?	700410490000000000010,490	70039320000000000009,320	7002429000000000000429^[31]	70032465000000000002,465	?	700432520000000000032,520	7002492524000000000492.524^[24]
Titanium	No	70031668000000000001,668	7002295600000000000295.6	70031273500000000001,273.5	69995235000000999990.5235	?	70034506000000000004,506	70034110000000000004,110	700121900000000000021.9^[32]	70032359000000000002,359	?	70037190000000000007,190	70008046900000000008.0469^[33]
Zinc	No	7002419539999900000419.53	7002112000000000000112.0	7002767500000000000767.5	69993896000000000000.3896	?	70037140000000000007,140	70036570000000000006,570	7002116000000000000116^[34]	70032782000000000002,782	?	700417960000000000017,960	70002157350000000002.15735^[24]
NaNO3	No	310	174										^[35]
NaNO2	No	282	212										^[35]
NaOH	No	318	158										^[35]
KNO3	No	337	116										^[35]
KOH	No	360	167										^[35]
NaOH/ Na2CO3 (7.2%)	No	283	340										^[35]
NaCl(26.8%)/NaOH	No	370	370										^[35]
NaCl/KCL(32.4%)/LiCl(32.8%)	No	346	281										^[35]
NaCl(5.7%)/ NaNO3 (85.5%)/Na2SO4	No	287	176										^[35]
NaCl/ NaNO3 (5.0%)	No	284	171										^[35]
NaCl(5.0%)/ NaNO3	No	282	212										^[35]
NaCl(42.5%)/KCl(20.5)/MgCl2	No	385-393	410										^[35]
KNO3(10%)/NaNO3	No	290	170										^[35]
KNO3/KCl(4,5%)	No	320	150										^[35]
KNO3/KBr(4.7%)/KCl(7.3%)	No	342	140										^[35]

Volumetric heat capacity (VHC) J·m⁻³·K⁻¹

$VHC=\rho c_{p}$

Thermal inertia (I) = Thermal effusivity (e) J·m⁻²·K⁻¹·s^−1/2

$I={\sqrt {k\rho c_{p}}}=e={(k\rho c_{p})}^{{1/2}}$

Technology, development and encapsulation

The most commonly used PCMs are salt hydrates, fatty acids and esters, and various paraffins (such as octadecane). Recently also ionic liquids were investigated as novel PCMs.

As most of the organic solutions are water-free, they can be exposed to air, but all salt based PCM solutions must be encapsulated to prevent water evaporation or uptake. Both types offer certain advantages and disadvantages and if they are correctly applied some of the disadvantages becomes an advantage for certain applications.

They have been used since the late 19th century as a medium for the thermal storage applications. They have been used in such diverse applications as refrigerated transportation^[36] for rail^[37] and road applications^[38] and their physical properties are, therefore, well known.

Unlike the ice storage system, however, the PCM systems can be used with any conventional water chiller both for a new or alternatively retrofit application. The positive temperature phase change allows centrifugal and absorption chillers as well as the conventional reciprocating and screw chiller systems or even lower ambient conditions utilizing a cooling tower or dry cooler for charging the TES system.

The temperature range offered by the PCM technology provides a new horizon for the building services and refrigeration engineers regarding medium and high temperature energy storage applications. The scope of this thermal energy application is wide ranging of solar heating, hot water, heating rejection, i.e. cooling tower and dry cooler circuitry thermal energy storage applications.

Since PCMs transform between solid–liquid in thermal cycling, encapsulation^[39] naturally become the obvious storage choice.

Encapsulation of PCMs
- Macro-encapsulation: Early development of macro-encapsulation with large volume containment failed due to the poor thermal conductivity of most PCMs. PCMs tend to solidify at the edges of the containers preventing effective heat transfer.
- Micro-encapsulation: Micro-encapsulation on the other hand showed no such problem. It allows the PCMs to be incorporated into construction materials, such as concrete, easily and economically. Micro-encapsulated PCMs also provide a portable heat storage system. By coating a microscopic sized PCM with a protective coating, the particles can be suspended within a continuous phase such as water. This system can be considered a phase change slurry (PCS).
- Molecular-encapsulation is another technology, developed by Dupont de Nemours that allows a very high concentration of PCM within a polymer compound. It allows storage capacity up to 515 kJ/m² for a 5 mm board (103 MJ/m³). Molecular-encapsulation allows drilling and cutting through the material without any PCM leakage.

As phase change materials perform best in small containers, therefore they are usually divided in cells. The cells are shallow to reduce static head – based on the principle of shallow container geometry. The packaging material should conduct heat well; and it should be durable enough to withstand frequent changes in the storage material's volume as phase changes occur. It should also restrict the passage of water through the walls, so the materials will not dry out (or water-out, if the material is hygroscopic). Packaging must also resist leakage and corrosion. Common packaging materials showing chemical compatibility with room temperature PCMs include stainless steel, polypropylene and polyolefin.

Thermal composites

Thermal-composites is a term given to combinations of phase change materials (PCMs) and other (usually solid) structures. A simple example is a copper-mesh immersed in a paraffin-wax. The copper-mesh within parraffin-wax can be considered a composite material, dubbed a thermal-composite. Such hybrid materials are created to achieve specific overall or bulk properties.

Thermal conductivity is a common property which is targeted for maximisation by creating thermal composites. In this case the basic idea is to increase thermal conductivity by adding a highly conducting solid (such as the copper-mesh) into the relatively low conducting PCM thus increasing overall or bulk (thermal) conductivity. If the PCM is required to flow, the solid must be porous, such as a mesh.

Solid composites such as fibre-glass or kevlar-pre-preg for the aerospace industry usually refer to a fibre (the kevlar or the glass) and a matrix (the glue which solidifies to hold fibres and provide compressive strength). A thermal composite is not so clearly defined, but could similarly refer to a matrix (solid) and the PCM which is of course usually liquid and/or solid depending on conditions.

Applications

Applications^[1]^[40] of phase change materials include, but are not limited to:

Thermal energy storage
Conditioning of buildings, such as 'ice-storage'
Cooling of heat and electrical engines
Cooling: food, beverages, coffee, wine, milk products, green houses
Medical applications: transportation of blood, operating tables, hot-cold therapies
Waste heat recovery
Off-peak power utilization: Heating hot water and Cooling
Heat pump systems
Passive storage in bioclimatic building/architecture (HDPE, paraffin)
Smoothing exothermic temperature peaks in chemical reactions
Solar power plants
Spacecraft thermal systems
Thermal comfort in vehicles
Thermal protection of electronic devices
Thermal protection of food: transport, hotel trade, ice-cream, etc.
Textiles used in clothing
Computer cooling
Turbine Inlet Chilling with thermal energy storage
Telecom shelters in tropical regions. They protect the high-value equipment in the shelter by keeping the indoor air temperature below the maximum permissible by absorbing heat generated by power-hungry equipment such as a Base Station Subsystem. In case of a power failure to conventional cooling systems, PCMs minimize use of diesel generators, and this can translate into enormous savings across thousands of telecom sites in tropics.

Fire and safety issues

Some phase change materials are suspended in water, and are relatively nontoxic. Others are hydrocarbons or other flammable materials, or are toxic. As such, PCMs must be selected and applied very carefully, in accordance with fire and building codes and sound engineering practices. Because of the increased fire risk, flamespread, smoke, potential for explosion when held in containers, and liability, it may be wise not to use flammable PCMs within residential or other regularly occupied buildings. Phase change materials are also being used in thermal regulation of electronics.

References

↑ 1.0 1.1 Kenisarin, M; Mahkamov, K (2007). "Solar energy storage using phase change materials". Renewable and Sustainable Energy Reviews 11 (9): 1913–1965. doi:10.1016/j.rser.2006.05.005.
↑ Sharma, Atul; Tyagi, V.V.; Chen, C.R.; Buddhi, D. (2009). "Review on thermal energy storage with phase change materials and applications". Renewable and Sustainable Energy Reviews 13 (2): 318–345. doi:10.1016/j.rser.2007.10.005.
↑ "Heat storage systems" (PDF) by Mary Anne White, brings a list of advantages and disadvantages of Paraffin heat storage. A more complete list can be found in AccessScience website from McGraw-Hill, DOI 10.1036/1097-8542.YB020415, last modified: March 25, 2002 based on 'Latent heat storage in concrete II, Solar Energy Materials, Hawes DW, Banu D, Feldman D, 1990, 21, pp.61–80.
↑ See above: 'Heat Storage Systems' (Mary Anne White), page 2
↑ Pasupathy, A; Velraj, R; Seeniraj, R (2008). "Phase change material-based building architecture for thermal management in residential and commercial establishments". Renewable and Sustainable Energy Reviews 12: 39–64. doi:10.1016/j.rser.2006.05.010.
↑ HyperPhysics, most from Young, Hugh D., University Physics, 7th Ed., Addison Wesley, 1992. Table 15-5. (most data should be at 293 K (20 °C; 68 °F))
↑ Ice – Thermal Properties. Engineeringtoolbox.com. Retrieved on 2011-06-05.
↑ AAP (April 21, 2009). "Melburnians face 60pc water cost rise - MELBURNIANS face paying up to 60 per cent more for water and sewerage under proposals announced today by the state's economic regulator.". The Australian. Retrieved 2010-02-24.
↑ http://www.alibaba.com/trade/search?fsb=y&IndexArea=product_en&CatId=&SearchText=sodium+sulfate
↑ http://www.alibaba.com/trade/search?fsb=y&IndexArea=product_en&CatId=&SearchText=sodium+sulfate
↑ 11.0 11.1 Sarı, A (2002). "Thermal and heat transfer characteristics in a latent heat storage system using lauric acid". Energy Conversion and Management 43 (18): 2493–2507. doi:10.1016/S0196-8904(01)00187-X.
↑ 12.0 12.1 H. Kakuichi et al., IEA annex 10 (1999)
↑ Beare-Rogers, J.; Dieffenbacher, A.; Holm, J.V. (2001). "Lexicon of lipid nutrition (IUPAC Technical Report)". Pure and Applied Chemistry 73 (4): 685–744. doi:10.1351/pac200173040685.
↑ "lauric acid Q/MHD002-2006 lauric acid CN;SHN products". Alibaba.com. Retrieved 2010-02-24.
↑ "Fatty Acids – Fractioned (Asia Pacific) Price Report – Chemical pricing information". ICIS Pricing. Retrieved 2010-03-10.
↑ 16.0 16.1 Nagano, K (2003). "Thermal characteristics of manganese (II) nitrate hexahydrate as a phase change material for cooling systems". Applied Thermal Engineering 23 (2): 229–241. doi:10.1016/S1359-4311(02)00161-8.
↑ 17.0 17.1 Yinping, Zhang; Yi, Jiang; Yi, Jiang (1999). Measurement Science and Technology 10 (3): 201–205. Bibcode:1999MeScT..10..201Y. doi:10.1088/0957-0233/10/3/015.
↑ Kalapathy, Uruthira; Proctor, Andrew; Shultz, John (2002-12-10). "Silicate Thermal Insulation Material from Rice Hull Ash". Industrial & Engineering Chemistry Research 42 (1): 46–49. doi:10.1021/ie0203227.
↑ Sodium Silicate (Water Glass). Sheffield-pottery.com. Retrieved on 2011-06-05.
↑ Hukseflux Thermal Sensors. Hukseflux.com. Retrieved on 2011-06-05.
↑ Aluminium. Goodefellow. Web.archive.org (2008-11-13). Retrieved on 2011-06-05.
↑ "Aluminum Prices, London Metal Exchange (LME) Aluminum Alloy Prices, COMEX and Shanghai Aluminum Prices". 23 February 2010. Retrieved 2010-02-24.
↑ Copper. Goodfellow. Web.archive.org (2008-11-16). Retrieved on 2011-06-05.
↑ 24.0 24.1 24.2 24.3 24.4 "Metal Prices and News". 23 February 2010. Retrieved 2010-02-24.
↑ Gold. Goodfellow. Web.archive.org (2008-11-15). Retrieved on 2011-06-05.
↑ Iron. Goodfellow. Web.archive.org (2008-11-18). Retrieved on 2011-06-05.
↑ "Iron Page". 7 December 2007. Retrieved 2010-02-24.
↑ Lead. Goodfellow. Web.archive.org (2008-11-18). Retrieved on 2011-06-05.
↑ Lithium. Goodfellow. Web.archive.org (2008-11-18). Retrieved on 2011-06-05.
↑ "Historical Price Query". August 14, 2009. Retrieved 2010-02-24.
↑ Silver. Goodfellow. Web.archive.org (2008-11-17). Retrieved on 2011-06-05.
↑ Titanium. Goodfellow. Web.archive.org (2008-11-15). Retrieved on 2011-06-05.
↑ "Titanium Page". 28 December 2007. Retrieved 2010-02-24.
↑ Zinc. Goodfellow. Web.archive.org (2008-11-18). Retrieved on 2011-06-05.
↑ 35.0 35.1 35.2 35.3 35.4 35.5 35.6 35.7 35.8 35.9 35.10 35.11 35.12 35.13 35.14 http://www.nrel.gov/csp/troughnet/pdfs/tamme_phase_change_storage_systems.pdf
↑ Frederik Tudor the Ice King on ice transport during the 19th century
↑ Richard Trevithick's steam locomotive ran in 1804
↑ Amédée Bollée created steam cars beginning at 1873
↑ Tyagi, Vineet Veer; Buddhi, D. (2007). "PCM thermal storage in buildings: A state of art". Renewable and Sustainable Energy Reviews 11 (6): 1146–1166. doi:10.1016/j.rser.2005.10.002.
↑ Omer, A (2008). "Renewable building energy systems and passive human comfort solutions". Renewable and Sustainable Energy Reviews 12 (6): 1562–1587. doi:10.1016/j.rser.2006.07.010.