Magnetocrystalline anisotropy

From Wikipedia, the free encyclopedia

In physics, a ferromagnetic material is said to have magnetocrystalline anisotropy if it takes more energy to magnetize it in certain directions than in others. These directions are usually related to the principal axes of its crystal lattice. It is a special case of magnetic anisotropy.

Causes

The spin-orbit interaction is the primary source of magnetocrystalline anisotropy.

Practical relevance

Magnetocrystalline anisotropy has a great influence on industrial uses of ferromagnetic materials. Materials with high magnetic anisotropy usually have high coercivity; that is they are hard to demagnetize. These are called "hard" ferromagnetic materials, and are used to make permanent magnets. For example, the high anisotropy of rare earth metals is mainly responsible for the strength of rare earth magnets. During manufacture of magnets, a powerful magnetic field aligns the microcrystalline grains of the metal so their "easy" axes of magnetization all point in the same direction, freezing a strong magnetic field into the material.

On the other hand, materials with low magnetic anisotropy usually have low coercivity, their magnetization is easy to change. These are called "soft" ferromagnets, and are used to make magnetic cores for transformers and inductors. The small energy required to turn the direction of magnetization minimizes core losses, energy dissipated in the transformer core when the alternating current changes direction.

Microscopic origin

Magnetocrystalline anisotropy arises mostly from spin-orbit coupling.^[1] This effect is weak compared to the exchange interaction and is difficult to compute from first principles, although some successful computations have been made.^[2]

Thermodynamic theory

The magnetocrystalline anisotropy energy is generally represented as an expansion in powers of the direction cosines of the magnetization. The magnetization vector can be written $<var>M</var> = <var>M s </var>(<var> α, β, γ </var>)$ , where $<var>M</var> s$ is the saturation magnetization. Because of time reversal symmetry, only even powers of the cosines are allowed.^[3] The nonzero terms in the expansion depend on the crystal system (e.g., cubic or hexagonal).^[3] The order of a term in the expansion is the sum of all the exponents of magnetization components, i.e., $<var> α β </var>$ is second order.

Uniaxial anisotropy

A representation of a uniaxial easy axis and easy plane. Arrows represent possible magnetization directions, black for the easy axis and red for the plane.

More than one kind of crystal system has a single axis of high symmetry (threefold, fourfold or sixfold). The anisotropy of such crystals is called uniaxial anisotropy. If the $<var>z</var>$ axis is taken to be the main symmetry axis of the crystal, the lowest order term in the energy is^[4]

$E/V=K_{1}\left(\alpha ^{2}+\beta ^{2}\right)=K_{1}\left(1-\gamma ^{2}\right).$ ^[5]

The ratio $<var>E/V</var>$ is an energy density (energy per unit volume). This can also be represented in spherical polar coordinates with $<var> α </var> = cos <var> φ </var> sin <var> θ </var>$ , $<var> β </var> = sin <var> φ </var> sin <var> θ </var>$ , and $<var> γ </var> = cos <var> θ </var>$ :

$\displaystyle E/V=K_{1}\sin ^{2}\theta .$

The parameter $<var>K</var> 1$ , often represented as $<var>K</var> u$ , has units of energy density and depends on composition and temperature.

The minima in this energy with respect to $<var> θ </var>$ satisfy

${\frac {\partial E}{\partial \theta }}=0\qquad {\text{and}}\qquad {\frac {\partial ^{2}E}{\partial \theta ^{2}}}>0.$

If $<var>K</var> 1 > 0$ , the directions of lowest energy are the $\pm <var>z</var>$ directions. The $<var>z</var>$ axis is called the easy axis. If $<var>K</var> 1 < 0$ , there is an easy plane perpendicular to the symmetry axis (the basal plane of the crystal).

Many models of magnetization represent the anisotropy as uniaxial and ignore higher order terms. However, if $<var>K</var> 1 < 0$ , the lowest energy term does not determine the direction of the easy axes within the basal plane. For this, higher-order terms are needed, and these depend on the crystal system (hexagonal, tetragonal or rhombohedral).^[3]

The hexagonal lattice cell.
The tetragonal lattice cell.
The rhombohedral lattice cell.

Hexagonal system

A representation of an easy cone. All the minimum-energy directions (such as the arrow shown) lie on this cone.

In a hexagonal system the $<var>c</var>$ axis is an axis of sixfold rotation symmetry. The energy density is, to fourth order,

$\displaystyle E/V=K_{1}\sin ^{2}\theta +K_{2}\sin ^{4}\theta +K_{3}\sin ^{4}\theta \cos 6\phi$ .

The uniaxial anisotropy is mainly determined by the first two terms. Depending on the values $<var>K</var> 1$ and $<var>K</var> 2$ , there are four different kinds of anisotropy (isotropic, easy axis, easy plane and easy cone):^[6]

$<var>K</var> 1 = <var>K</var> 2 = 0$ : the ferromagnet is isotropic.
$<var>K</var> 1 > 0$ and $<var>K</var> 2 > -<var>K</var> 1$ : the $<var>c</var>$ axis is an easy axis.
$<var>K</var> 1 > 0$ and $<var>K</var> 2 < -<var>K</var> 1$ : the basal plane is an easy plane.
$<var>K</var> 1 < 0$ and $<var>K</var> 2 < -<var>K</var> 1 /2$ : the basal plane is an easy plane.
$-2<var>K</var> 2 < <var>K</var> 1 < 0$ : the ferromagnet has an easy cone (see figure to right).

The basal plane anisotropy is determined by the third term, which is sixth-order. The easy directions are projected onto three axes in the basal plane.

Below are some room-temperature anisotropy constants for hexagonal ferromagnets. Since all the values of $<var>K</var> 1$ and $<var>K</var> 2$ are positive, these materials have an easy axis.

Room-temperature anisotropy constants ( $\times 104 J/m 3$ ). ^[1]
Structure	$K_{1}$	$K_{2}$
Co	$45$	$15$
αFe₂O₃ (hematite)	$120$ ^[7]
Ba O· 6Fe₂O₃	$3$
Y Co₅	$550$
Mn Bi	$89$	$27$

Higher order constants, in particular conditions, may lead to first order magnetization processes FOMP.

Tetragonal and Rhombohedral systems

The energy density for a tetragonal crystal is^[3]

$\displaystyle E/V=K_{1}\sin ^{2}\theta +K_{2}\sin ^{4}\theta +K_{3}\sin ^{4}\theta \sin 2\phi$ .

Note that the $<var>K</var> 3$ term, the one that determines the basal plane anisotropy, is fourth order (same as the $<var>K</var> 2$ term). The definition of $<var>K</var> 3$ may vary by a constant multiple between publications.

The energy density for a rhombohedral crystal is^[3]

$\displaystyle E/V=K_{1}\sin ^{2}\theta +K_{2}\sin ^{4}\theta +K_{3}\cos \theta \sin ^{3}\theta \cos 3\phi$ .

Cubic anisotropy

Energy surface for cubic anisotropy with

<var>K</var> 1 > 0

. Both color saturation and distance from the origin increase with energy. The lowest energy (lightest blue) is arbitrarily set to zero.

Energy surface for cubic anisotropy with

<var>K</var> 1 < 0

. Same conventions as for

<var>K</var> 1 > 0

In a cubic crystal the lowest order terms in the energy are^[3]^[1]

$E/V=K_{1}\left(\alpha ^{2}\beta ^{2}+\beta ^{2}\gamma ^{2}+\gamma ^{2}\alpha ^{2}\right)+K_{2}\alpha ^{2}\beta ^{2}\gamma ^{2}.$

If the second term can be neglected, the easy axes are the $< 100 >$ axes (i.e., the $\pm <var>x</var>$ , $\pm <var>y</var>$ , and $\pm <var>z</var>$ , directions) for $<var>K</var> 1 > 0$ and the $< 111 >$ directions for $<var>K</var> 1 < 0$ (see images on right).

If $<var>K</var> 2$ is not assumed to be zero, the easy axes depend on both $<var>K</var> 1$ and $<var>K</var> 2$ . These are given in the table below, along with hard axes (directions of greatest energy) and intermediate axes (saddle points) in the energy). In energy surfaces like those on the right, the easy axes are analogous to valleys, the hard axes to peaks and the intermediate axes to mountain passes.

Easy axes for $<var>K</var> 1 > 0$ . ^[1]
Type of axis	$K_{2}=+\infty$ to $-9K_{1}/4$	$K_{2}=-9K_{1}/4$ to $-9K_{1}$	$K_{2}=-9K_{1}$ to $-\infty$
Easy	$\langle 100\rangle$	$\langle 100\rangle$	$\langle 111\rangle$
Medium	$\langle 110\rangle$	$\langle 111\rangle$	$\langle 100\rangle$
Hard	$\langle 111\rangle$	$\langle 110\rangle$	$\langle 110\rangle$

Easy axes for $<var>K</var> 1 < 0$ . ^[1]
Type of axis	$K_{2}=+\infty$ to $-9K_{1}/4$	$K_{2}=-9K_{1}/4$ to $-9K_{1}$	$K_{2}=-9K_{1}$ to $-\infty$
Easy	$\langle 111\rangle$	$\langle 110\rangle$	$\langle 110\rangle$
Medium	$\langle 110\rangle$	$\langle 111\rangle$	$\langle 100\rangle$
Hard	$\langle 100\rangle$	$\langle 100\rangle$	$\langle 111\rangle$

Below are some room-temperature anisotropy constants for cubic ferromagnets. The compounds involving Fe₂O₃ are ferrites, an important class of ferromagnets. In general the anisotropy parameters for cubic ferromagnets are higher than those for uniaxial ferromagnets. This is consistent with the fact that the lowest order term in the expression for cubic anisotropy is fourth order, while that for uniaxial anisotropy is second order.

Room-temperature anisotropy constants ( $\times 104 J/m 3$ ). ^[1]
Structure	$K_{1}$	$K_{2}$
Fe	$4.8$	$\pm 0.5$
Ni	$-0.5$	$-0.2$
Fe O· Fe₂O₃ (magnetite)	$-1.1$
Mn O· Fe₂O₃	$-0.3$
Ni O· Fe₂O₃	$-0.62$
Mg O· Fe₂O₃	$-0.25$
Co O· Fe₂O₃	$20$

Temperature dependence of anisotropy

The magnetocrystalline anisotropy parameters have a strong dependence on temperature. They generally decrease rapidly as the temperature approaches the Curie temperature, so the crystal becomes effectively isotropic.^[1] Some materials also have an isotropic point at which $<var>K</var> 1 = 0$ . Magnetite (Fe₃O₄), a mineral of great importance to rock magnetism and paleomagnetism, has an isotropic point at 130 kelvin.^[7]

Magnetite also has a phase transition at which the crystal symmetry changes from cubic (above) to monoclinic or possibly triclinic below. The temperature at which this occurs, called the Verwey temperature, is 120 Kelvin.^[7]

Magnetostriction

The magnetocrystalline anisotropy parameters are generally defined for ferromagnets that are constrained to remain undeformed as the direction of magnetization changes. However, coupling between the magnetization and the lattice does result in deformation, an effect called magnetostriction. To keep the lattice from deforming, a stress must be applied. If the crystal is not under stress, magnetostriction alters the effective magnetocrystalline anisotropy. If a ferromagnet is single domain (uniformly magnetized), the effect is to change the magnetocrystalline anisotropy parameters.^[8]

In practice, the correction is generally not large. In hexagonal crystals, there is no change in $<var>K</var> 1$ .^[9] In cubic crystals, there is a small change, as in the table below.

Room-temperature anisotropy constants $<var>K</var> 1$ (zero-strain) and $<var>K</var> 1'$ (zero-stress) ( $\times 104 J/m 3$ ). ^[9]
Structure	$K_{1}$	$K'_{1}$
Fe	$4.7$	$4.7$
Ni	$-6.0$	$-5.9$
Fe O· Fe₂O₃ (magnetite)	$-1.1$	$-1.4$

Notes and references

↑ 1.0 1.1 1.2 1.3 1.4 1.5 1.6 Cullity & Graham 2005
↑ Daalderop, Kelly & Schuurmans 1990
↑ 3.0 3.1 3.2 3.3 3.4 3.5 Landau, Lifshitz & Pitaevski 2004
↑ An arbitrary constant term is ignored.
↑ The lowest-order term in the energy can be written in more than one way because, by definition, $<var> α 2 + β 2 + γ 2 <var> = 1$ .
↑ Cullity & Graham 2005, p. 7-7
↑ 7.0 7.1 7.2 Dunlop & Özdemir 1997
↑ Chikazumi 1997, chapter 12
↑ 9.0 9.1 Ye, Newell & Merrill 1994