Polyvinyl alcohol
From Wikipedia, the free encyclopedia
 |
This article needs additional citations for verification. Please help improve this article by adding reliable references. Unsourced material may be challenged and removed. (August 2007) |
| Polyvinyl alcohol | |
|---|---|
 |
|
| Other names | PVOH; Ethenol, homopolymer; PVA; Polyviol; Vinol; Alvyl; Alkotex; Covol; Gelvatol; Lemol; |
| Identifiers | |
| CAS number | [9002-89-5] |
| RTECS number | TR8100000 |
| Properties | |
| Molecular formula | (C2H4O)x |
| Density | 1.19-1.31 g/cm³ |
| Melting point |
230°C |
| Boiling point |
228°C |
| Hazards | |
| MSDS | External MSDS |
| NFPA 704 |
 2
0
0
|
| Flash point | 79.44°C |
| LD50 | 14,700 mg/kg (Mouse) |
| Except where noted otherwise, data are given for materials in their standard state (at 25 °C, 100 kPa) Infobox disclaimer and references |
|
Polyvinyl alcohol (PVOH, PVA, or PVAL) is a water-soluble synthetic polymer.
Contents |
[edit] Properties
Polyvinyl alcohol has excellent film forming, emulsifying, and adhesive properties. It is also resistant to oil, grease and solvent. It is odorless and nontoxic. It has high tensile strength and flexibility, as well as high oxygen and aroma barrier properties. However these properties are dependent on humidity, in other words, with higher humidity more water is absorbed. The water, which acts as a plasticiser, will then reduce its tensile strength, but increase its elongation and tear strength. PVA is fully degradable and is a quick dissolver. It is odourless and non toxic. PVA has a melting point of 230°C and 180–190°C for the fully hydrolysed and partially hydrolysed grades. It decomposes rapidly above 200°C as it can undergo pyrolysis at high temperatures.
PVA is an atactic material but exhibits crystallinity as the hydroxyl groups are small enough to fit into the lattice without disrupting it.
[edit] Uses
Some uses of polyvinyl alcohol include:
- Adhesive and thickener material in latex paints, paper coatings, hairsprays, shampoos and glues.
- Carbon dioxide barrier in polyethylene terephthalate (PET) bottles.
- Carotid phantoms for use as synthetic vessels in doppler flow testing.
- Children's play putty or slime when combined with borax.
- Feminine hygiene and adult incontinence products as a biodegradable plastic backing sheet.
- As a mold release because materials such as epoxy do not stick to it.
- As a water-soluble film useful for packaging.
- As fiber reinforcement in concrete
- As a surfactant for the formation of polymer encapsulated nanobeads
- Used with polyvinyl acetate to make Elmer's glue
- Used in eye drops and hard contact lens solution as a lubricant.
- Used in protective chemical-resistant gloves
- Used as a fixative for specimen collection, especially stool samples
- When doped with iodine, PVA can be used to polarize light.
[edit] Fishing
PVA is widely used in freshwater sport fishing. Small bags made from PVA are filled with dry- or oil-based bait and attached to the hook, or the baited hook is placed inside the bag and cast into the water. When the bag lands on the lake or river bottom it breaks down, leaving the hook bait surrounded by ground bait, pellets etc. This method helps attract fish to the hook bait, though it does result in dissolved plastic in the water.
Anglers also use string made of PVA for the purpose of making temporary attachments; for example holding in a coil a length of line that might otherwise tangle while the cast is made.
[edit] Production
There are over 22 producers worldwide with ~ 1 million tons on the open market in 2002. Larger producers include Kuraray (Japan) and Celanese (USA) but mainland China has installed a number of very large production facilities in the past decade.
[edit] Preparation
Unlike most vinyl polymers, PVA is not prepared by polymerization of the corresponding monomer. The monomer, vinyl alcohol, almost exclusively exists as the tautomeric form, acetaldehyde. PVA instead is prepared by partial or complete hydrolysis of polyvinyl acetate to remove acetate groups.