Metal-induced gap states

From Wikipedia, the free encyclopedia


In bulk semiconductor band structure calculations, it is assumed that the crystal lattice (which features a periodic potential due to the atomic structure) of the material is infinite. When the finite size of a crystal is taken into account, the wavefunctions of electrons are altered and states that are forbidden within the bulk semiconductor gap are allowed at the surface. Similarly, when a metal is deposited onto a semiconductor (by thermal evaporation (deposition), for example), the wavefunction of an electron in the semiconductor must match that of an electron in the metal at the interface. Since the Fermi levels of the two materials must match at the interface, there exists gap states that decay deeper into the semiconductor.

Contents

[edit] Band-Bending at the metal-semiconductor interface

Diagram of the band-bending at the interface of (a) a high work function metal and n-type semiconductor, (b) a high work function metal and a p-type semi conductor, (c)a lowhigh work function metal and a n-type semi conductor, (d)a low work function metal and a p-type semi conductor. (Figure adapted from H. Luth's Solid Surfaces, Interfaces, and Thin Films, p. 384.)
Diagram of the band-bending at the interface of (a) a high work function metal and n-type semiconductor, (b) a high work function metal and a p-type semi conductor, (c)a lowhigh work function metal and a n-type semi conductor, (d)a low work function metal and a p-type semi conductor. (Figure adapted from H. Luth's Solid Surfaces, Interfaces, and Thin Films, p. 384.[1])

As mentioned above, when a metal is deposited onto a semiconductor, even when the metal film is smaller than a single atomic layer, the Fermi levels of the metal and semiconductor must match. This pins the Fermi level in the semiconductor to a position in the bulk gap. Shown to the right is a diagram of band-bending interfaces between two different metals (high and low work functions) and two different semiconductors (n-type and p-type).

Volker Heine was one of the first to respect the length of the tail end of metal electron states extending into the semiconductor's energy gap. He calculated the variation in surface state energy by matching wavefunctions of a free-electron metal to gapped states in an undoped semiconductor, showing that in most cases the position of the surface state energy is quite stable regardless of the metal used.[2]

[edit] Branching point

It is somewhat crude to suggest that the MIGS are tail ends of metal states that leak into the semiconductor. Since the mid-gap states do exist within some depth of the semiconductor, they must be a mixture (a Fourier series) of valence and conduction band states from the bulk. The resulting positions of these states, as calculated by J. Tersoff [3][4], must be closer to either the valence- or conduction- band thus acting as acceptor or donor dopants, respectively. The point that divides these two types of MIGS is called the branching point, E_B. Tersoff argued

 E_B = \frac{1}{2}[\bar{E_V} + \bar{E_C}]
 \bar{E_V} = E_V - \frac{1}{3} \Delta_{so} , where Δso is the spin orbit splitting of EV at the Γ point.
 \bar{E_C} is the indirect conduction band minimum.

[edit] Metal/Semiconductor contact point barrier height

Diagram of the contact point potential barrier at the interface of a metal and semiconductor.  Shown are eΦbh, the energy of the barrier, and eVif, the maximum band bending in the semiconductor. (Figure adapted from H. Luth's Solid Surfaces, Interfaces, and Thin Films, p. 408 (see Refs.)
Diagram of the contact point potential barrier at the interface of a metal and semiconductor. Shown are eΦbh, the energy of the barrier, and eVif, the maximum band bending in the semiconductor. (Figure adapted from H. Luth's Solid Surfaces, Interfaces, and Thin Films, p. 408 (see Refs.)

In order for the Fermi levels to match at the interface, there must be charge transfer between the metal and semiconductor. The amount of charge transfer was formulated by Linus Pauling [5] and later revised [6] to be:

\delta q = \frac{0.16}{eV}|X_M - X_{SC}| + \frac{0.035}{eV^2}|X_M - X_{SC}|^2

where XM and XSC are the electronegativities of the metal and semiconductor, respectively. The charge transfer produces a dipole at the interface and thus a potential barrier called the Schottky barrier height. In the same derivation of the branching point mentioned above, Tersoff derives the barrier height to be:

\Phi_{bh} = \frac{1}{2}[\bar{E_C} - \bar{E_V}] + \delta_m = \frac{1}{2} [\bar{E_C} - E_V - \frac{\Delta_{so}}{3}] + \delta_m

where δm is a parameter adjustable for the specific metal, dependent mostly on its electronegativity, XM. Tersoff showed that the experimentally measured phi_bp fits his theoretical model for Au in contact with 10 common semiconductors, including Si, Ge, GaP, and GaAs.

Another derivation of the contact barrier height in terms of experimentally measurable parameters was worked out by Federico Garcia-Moliner who considered the density of states and dipole contributions more rigorously [7].

\Phi_{bh} = \frac{1}{1+\alpha N_{vs}} [\Phi_M - X_M + D_J + \alpha N_{vs}(E_g - \Phi_0)]
α is dependent on the charge densities of the both materials
Nvs = density of surface states
φM = work function of metal
DJ = sum of dipole contributions considering dipole corrections to the jellium model
EG = semiconductor gap
Φ0 Ef – Ev in semiconductor

Thus φbh can be calculated by theoretically deriving or experimentally measuring each parameter. Garcia-Moliner also discusses two limits

αNvs > > 1 (The Bardeen Limit), where the high density of interface states pins the Fermi level at that of the semiconductor regardless of ΦM.
αNvs < < 1 (The Schottky Limit)whereΦbh varies with strongly with the characteristics of the metal, including the particular lattice structure as accounted for in DJ.

[edit] Applications

When a bias voltage V is applied across the interface of an n-type semiconductor and a metal, the Fermi level in the semiconductor is shifted with respect to the metal's and the band bending decreases. In effect, the capacitance across the depletion layer in the semiconductor is bias voltage dependent and goes as (V_{if}-V)^{\frac{1}{2}}. This makes the metal/semiconductor junction useful in varactor devices used frequently in electronics.

[edit] References

  1. ^ H. Luth, Solid Surfaces, Interfaces, and Films, Springer-Verlag Berlin Heidelberg, New York, NY, 2001.
  2. ^ V. Heine, "Theory of Surface States," Phys. Rev., 138, A 1689 (1965).
  3. ^ J. Tersoff, "Theory of semiconductor heterojunctions: The role of quantum dipoles," Phys. Rev. B 30, 4874 (1984).
  4. ^ J. Tersoff, "Schottky barriers and semiconductor band structures," Phys. Rev. B 32, 6968 (1985).
  5. ^ L. Pauling, The Nature of the Chemical Bond. Cornell University Press, Ithaca, 1960.
  6. ^ N.B Hanney and C.P. Smith, "The Dipole Moment of Hydrogen Fluoride and the Ionic Character of Bonds," J. Am. Chem. Soc. 68, 171 (1946)
  7. ^ Garcia-Moliner, Federico, Introduction to the theory of solid surfaces, Cambridge University Press, Cambridge, London, 1979.