Cold saw blades are circular metal cutting saw blades categorized into two types: Solid High Speed Steel (HSS) or Tungsten Carbide-Tipped (TCT). Both types of blades are resharpenable and may be used many times before being discarded. Cold saw blades are used to cut metal using a relatively slow rotational speed, usually less than 5000 surface feet per minute (SFM) (25m/s), and a high chip load per tooth, usually between .001" - .003" (0.025 - 0.08mm) per tooth. These blades are driven by a high power motor and high-torque gear reduction unit or an AC vector drive. During the cutting process, the metal is released in a shearing action by the teeth as the blade turns and the feed mechanism moves the blade forward. They are called "cold saw blades" because they transfer all the energy and heat created during the cutting process to the chip. This enables the blade and the work material to remain cold.[1]
Contents |
[edit] Classification
The first type of cold saw blade, solid HSS, may be made from either M2 tool steel or M35 tool steel, alloyed with additional cobalt. Solid HSS saw blades are heat treated and hardened to 64/65 HRc for ferrous cutting applications and 58/60 HRc for non-ferrous cutting applications. This high rockwell hardness gives the cutting edges of the teeth a high resistance to heat and wear. However, this increased hardness also makes the blades brittle and not very resistant to shock. In order to produce a high quality HSS cold saw blade, you must start with very flat and properly tensioned raw material. The blades must be press quenched after hardening to prevent them from being warped. The term high speed steel (HSS) doesn't necessarily mean what it implies. These blades are usually never run at surface speeds higher than 350 SFM. Solid HSS cold saw blades may be used for cutting many different shapes and types of metal including: tubes, extrusions, structural sections, billets, bars, ingots, castings, forgings etc. These blades may also be coated with special wear resistant coatings such as Titanium Nitride (TiN) or Titanium Aluminum Nitride (TiAlN).
The second type of cold saw blade, Tungsten Carbide-Tipped (TCT), are made with an alloy steel body and tungsten carbide inserts brazed to the tips of the teeth. These tips are ground on all surfaces to create tangential and radial clearance and provide the proper cutting and clearance angles on the teeth. The alloy body is generally made from a wear resistant material such as a chrome vanadium steel, heat treated to 38/42 HRc . The tungsten carbide tips are capable of operating at much higher temperatures than solid HSS, therefore, TCT saw blades are usually run at much higher surface speeds. This allows carbide-tipped blades to cut at faster rates and still maintain an acceptable chip load per tooth. These blades are commonly used for cutting non-ferrous alloys, but have gained significant popularity for ferrous metal cutting applications in the last 10 years. The tungsten carbide inserts are extremely hard (98 HRc ) and capable of very long wear life. However, they are less resistant to shock than solid HSS cold saw blades. Any vibration during the cutting process may severely damage the teeth. These cold saw blades need to be driven by a backlash free gear box and a constant feed mechanism like a ball-screw feed.[2]
[edit] Future
The popularity of cold saw blades is increasing due to the technological advancements in cold saw machines. They are the sawing method of choice when high production requirements are needed. They consistently produce the lowest cost per cut among all sawing methods: hot sawing, friction sawing, bandsawing and hacksawing. [3]
[edit] See also
Cold Saw Circular Sawing Machine Used to Cut Metal
Friction & Hot Saw Blades August Blecher GmbH
Segmental Saw Blades
[edit] Notes
- ^ M2 HSS Saw Blades. Haas Saw & Supply.
- ^ TCT Cold Saw Blade. Gebr. Lennartz GmbH.
- ^ Cold Saw Blades. Peter J. Haas.