Polyketone

From Wikipedia, the free encyclopedia

Polyketone
Image:Polyketone.PNG
Density 140 kg/m3
Young's modulus(E) 1500 MPa
Tensile strengtht) 55 MPa
Elongation @ break 350%
notch test 20 kJ/m2
Glass temperature 15°C
melting point 220°C
Vicat B<1> 205
heat transfer coefficient (λ) 0.27 W/m.K
linear expansion coefficient (α) 11 10-5 /K
Specific heat (c) 1.8 kJ/kg.K
Water absorption (ASTM) 0.5
Price 3-5 €/kg
#   Deformation temperature at 10kN needle load
source: A.K. vam der Vegt & L.E. Govaert, Polymeren,
van keten tot kunstof, ISBN 90-407-2388-5

Polyketones are a family of high-performance thermoplastic polymers. The highly polar ketone groups in the polymer backbone of these materials gives rise to a strong attraction between polymer chains, which increases the material's melting point (255 degrees celsius for Carilon). Such materials also tend to resist solvents and have good mechanical properties. Unlike many other engineering plastics, aliphatic polyketones such as Shell's Carilon (where "R" in the diagram is an ethyl group) are relatively easy to synthesize and can be derived from inexpensive monomers. Carilon is made with a palladium(II) catalyst from ethylene and carbon monoxide. A small fraction of the ethylene is generally replaced with propylene to reduce the melting point somewhat.

For a discussion of the silicon containing polymers originally thought to have analogous structures, see silicone polymers.