Microelectromechanical systems
From Wikipedia, the free encyclopedia
Microelectromechanical Systems (MEMS) is the technology of the very small, and merges at the nanoscale into "Nanoelectromechanical" Systems (NEMS) and Nanotechnology.
MEMS are also referred to as micromechanics, micro machines, or Micro Systems Technology (MST). MEMS are separate and distinct from the hypothetical vision of Molecular nanotechnology or Molecular Electronics.
MEMS generally range in size from a micrometer (a millionth of a meter) to a millimeter (thousandth of a meter). At these size scales, the standard constructs of classical physics do not always hold true. Due to MEMS' large surface area to volume ratio, surface effects such as electrostatics and wetting dominate volume effects such as inertia or thermal mass.
They are fabricated using modified semiconductor fabrication technology (used to make electronics), molding and plating, wet etching (KOH, TMAH) and dry etching (RIE and DRIE), electro discharge machining (EDM), and other technologies capable of manufacturing very small devices.
Companies with strong MEMS programs come in many sizes. The larger firms specialize in manufacturing high volume inexpensive components or packaged solutions for end markets such as automobiles, biomedical, and electronics. The successful small firms provide value in innovative solutions and absorb the expense of custom fabrication with high sales margins. In addition, both large and small companies work in R&D to explore MEMS technology. Complexity and performance of advanced MEMS based sensors are described by different MEMS sensor generations.
Common applications include:
- inkjet printers, which use piezoelectrics or bubble ejection to deposit ink on paper.
- accelerometers in modern cars for a large number of purposes including airbag deployment in collisions.
- MEMS gyroscopes used in modern cars and other applications to detect yaw; e.g. to deploy a roll over bar or trigger dynamic stability control.
- pressure sensors e.g. car tire pressure sensors, and disposable blood pressure sensors.
- Displays e.g the DMD chip in a projector based on DLP technology has on its surface several hundred thousand micromirrors.
- Optical switching technology which is used for switching technology for data communications, and is part of the emerging technology of smartdust.
The motion-sensing controller in the Nintendo Wii video game system represents a popular consumer application of MEMS technology.
Finite element analysis is an important part of MEMS design.
Contents |
[edit] MEMS materials
MEMS technology can be implemented using a number of different materials and manufacturing techniques; the choice of which will depend on the device being created and the market sector in which it has to operate.
[edit] Silicon
Silicon is the material used to create most integrated circuits used in consumer electronics in the modern world. The economies of scale, ready availability of cheap high-quality materials and ability to incorporate electronic functionality make silicon attractive for a wide variety of MEMS applications. Silicon also has significant advantages engendered through its material properties. In single crystal form, silicon is an almost perfect Hookean material, meaning that when it is flexed there is virtually no hysteresis and hence almost no energy dissipation. As well as making for highly repeatable motion, this also makes silicon very reliable as it suffers very little fatigue and can have service lifetimes in the range of billions to trillions of cycles without breaking. The basic techniques for producing all silicon based MEMS devices are deposition of material layers, patterning of these layers by lithography and then etching to produce the required shapes.
[edit] Polymers
Even though the electronics industry provides an economy of scale for the silicon industry, crystalline silicon is still a complex and relatively expensive material to produce. Polymers on the other hand can be produced in huge volumes, with a great variety of material characteristics. MEMS devices can be made from polymers by processes such as injection moulding, embossing or stereolithography and are especially well suited to microfluidic applications such as disposable blood testing cartridges.
[edit] Metals
Metals can also be used to create MEMS elements. While metals do not have some of the advantages displayed by silicon in terms of mechanical properties, when used within their limitations, metals can exhibit very high degrees of reliability.
Metals can be deposited by electroplating, evaporation, and sputtering processes.
Commonly used metals include Gold, Nickel, Aluminum, Chromium, Titanium, Tungsten, Platinum and Silver.
[edit] MEMS processes
[edit] Deposition processes
One of the basic building blocks in MEMS processing is the ability to deposit thin films of material. In this text we assume a thin film to have a thickness anywhere between a few nanometers to about 100 micrometers. Commonly used deposition processes are: Electroplating, Sputter deposition, Physical Vapour Deposition (PVD) and Chemical Vapour Deposition (CVD). The Chemical Vapor Deposition Process is a very intricate process which takes place in several steps.
[edit] Photolithography
Main article: Photolithography
Lithography in MEMS context is typically the transfer of a pattern to a photosensitive material by selective exposure to a radiation source such as light. A photosensitive material is a material that experiences a change in its physical properties when exposed to a radiation source. If we selectively expose a photosensitive material to radiation (e.g. by masking some of the radiation) the pattern of the radiation on the material is transferred to the material exposed, as the properties of the exposed and unexposed regions differs.
This exposed region can then be removed or treated providing a mask for the underlying substrate. Photolithography is typically used with metal or other thin film deposition, wet and dry etching.
[edit] Etching processes
There are two basic categories of etching processes: wet and dry etching. In the former, the material is dissolved when immersed in a chemical solution. In the latter, the material is sputtered or dissolved using reactive ions or a vapor phase etchant.
[edit] Wet etching
Main article: Wet etching
Wet chemical etching consists in a selective removal of material by dipping a substrate into a solution that can dissolve it. Due to the chemical nature of this etching process, a good selectivity can often be obtained, which means that the etching rate of the target material is considerably higher than that of the mask material if selected carefully.
Some single crystal materials, such as silicon, will have different etching rates depending on the crystallographic orientation of the substrate. One of the most common examples is the etching of silicon in KOH (potassium hydroxide), where Si <111> planes etch approximately 100 times slower than other planes (crystallographic orientations). Therefore, etching a rectangular hole in a (100)-Si wafer will result in a pyramid shaped etch pit with 54.7° walls, instead of a hole with curved sidewalls as it would be the case for isotropic etching, where etching progresses at the same speed in all directions. Long and narrow holes in a mask will produce v-shaped grooves in the silicon. The surface of these grooves can be atomically smooth if the etch is carried out correctly, with dimensions and angles being extremely accurate.
Another method to change the etchant selectivity of silicon is to heavily dope the desired pattern with boron. This makes the silicon/boron unetchable to silicon etches. This technique is termed an 'etchstop'. See footnote for further information. Footnote: http://www.techneglas.com/dopantpages/etch.htm
[edit] Reactive ion etching (RIE)
Main article: Reactive ion etching
In reactive ion etching (RIE), the substrate is placed inside a reactor in which several gases are introduced. A plasma is struck in the gas mixture using an RF power source, breaking the gas molecules into ions. The ions are accelerated towards, and reacts at, the surface of the material being etched, forming another gaseous material. This is known as the chemical part of reactive ion etching. There is also a physical part which is similar in nature to the sputtering deposition process. If the ions have high enough energy, they can knock atoms out of the material to be etched without a chemical reaction. It is a very complex task to develop dry etch processes that balance chemical and physical etching, since there are many parameters to adjust. By changing the balance it is possible to influence the anisotropy of the etching, since the chemical part is isotropic and the physical part highly anisotropic the combination can form sidewalls that have shapes from rounded to vertical. A schematic of a typical reactive ion etching system is shown in the figure below.
[edit] Deep reactive ion etching (DRIE)
Main article: Deep reactive ion etching
A special subclass of RIE which continues to grow rapidly in popularity is deep RIE (DRIE). In this process, etch depths of hundreds of micrometres can be achieved with almost vertical sidewalls. The primary technology is based on the so-called "Bosch process", named after the German company Robert Bosch which filed the original patent, where two different gas compositions are alternated in the reactor. The first gas composition creates a polymer on the surface of the substrate, and the second gas composition etches the substrate. The polymer is immediately sputtered away by the physical part of the etching, but only on the horizontal surfaces and not the sidewalls. Since the polymer only dissolves very slowly in the chemical part of the etching, it builds up on the sidewalls and protects them from etching. As a result, etching aspect ratios of 50 to 1 can be achieved. The process can easily be used to etch completely through a silicon substrate, and etch rates are 3-4 times higher than wet etching.
[edit] Silicon MEMS paradigms
[edit] Bulk micromachining
Main article: Bulk micromachining
Bulk micromachining is the oldest paradigm of silicon based MEMS. The whole thickness of a silicon wafer is used for building the micro-mechanical structures. Silicon is machined using wet etching. Anodic bonding of glass plates to silicon is used for adding features in the third dimension and for hermetical encapsulation. Bulk micromachining has been essential in enabling high performance pressure sensors and accelerometers that have changed the shape of the sensor industry in the 80's and 90's.
[edit] Surface micromachining
Main article: Surface micromachining
Surface micromachining was created in the late 80's to render micromachining of silicon more planar, to make it resemble more the planar integrated circuit technology. The ultimate hope was that MEMS and integrated circuits could be combined on the same silicon wafer. The original surface micromachining concept was based on thin polycrystalline silicon layers used as movable mechanical structures and releasing them by sacrificial etching of the underlaying oxide layer. Interdigital comb electrodes were used to produce in-plane forces and to detect in-plane movement capacitively. This MEMS paradigm has enabled to manufacture low cost accelerometers for e.g. automotive air-bag systems and other applications where low performance and/ or high g-ranges are sufficient. Analog Devices have pioneered the industrialization of surface micromachining and have realized the co-integration of MEMS and integrated circuits.
[edit] High aspect ratio (HAR) micromachining
Both bulk and surface micromachining are still used in industrial production of sensors, ink-jet nozzles and other devices. But in many cases the distinction between these two has diminished. New etching technology, deep reactive ion etching has made it possible to combine good performance typical to bulk micromachining with comb structures and in-plane operation typical to surface micromachining. While it is common in surface micromachining to have structural layer thickness in the range of 2 µm, in HAR micromachining the thickness is from 10 to 100 µm. The materials commonly used in HAR micromachining are thick polycrystalline silicon, known as epi-poly, and bonded silicon-on-insulator (SOI) wafers although processes for bulk silicon wafer also have been created (SCREAM). Bonding a second wafer by glass frit bonding, anodic bonding or alloy bonding is used to protect the MEMS structures. Integrated circuits are typically not combined with HAR micromachining. The consensus of the industry at the moment seems to be that the flexibility and reduced process complexity obtained by having the two functions separated far outweighs the small penalty in packaging.
[edit] See also
- NEMS, Nanoelectromechanical systems are similar to MEMS but smaller
- MOEMS, Micro Opto-Electrical-Mechanical Systems, MEMS including optical elements
- Micropower Hydrogen generators, gas turbines, and electrical generators made of etched silicon
- IBM Millipede, a MEMS technology for non-volatile data storage of more than a terabit per square inch
- STMicroelectronics for 2x and 3x accelerometers
- Texas Instruments pioneers of the DMD chip
- ADI one of the major early players in accelerometer development
- Lucent who developed highly advanced optical telecommunications switches
- Cantilever one of the most common forms of MEMS.
- MEMS Thermal Actuator MEMS actuation created by thermal expansion
- Electrostatic motors used where coils are difficult to fabricate
[edit] External links
- The MEMS and Nanotechnology Clearinghouse (Information Source)
- memx.com Image Gallery
- Introduction and resources on MEMS and Microtechnology
- memscyclopedia.org A (not so) short introduction to MEMS
- MEMS process catalog - database of processes for the fabrication of MEMS devices